ABSTRACT
This study explores the tensile strength of adhesive joints in steel, focusing on the influence of heat treatment and diverse surface modifications. Results indicate a notable relationship between annealing temperature and tensile strength, with the most favorable outcomes identified at 90 min and 165 °C. Particularly, surfaces treated through turning, sandblasting, and plasma treatment (type C) consistently outperformed other methods. A standout revelation emerged from the turned, sandblasted, and plasma-treated surface (C), showcasing an exceptional tensile strength of 69.06 MPa. Load-holding tests underscored its resilience under diverse load conditions. Surface analyses, including roughness measurements, wetting characteristics, and Scanning Electron Microscope imaging, provided valuable insights into structural transformations induced by different treatments. Chemical composition examinations unveiled significant alterations post-plasma treatment, impacting surface chemistry and contributing to an outstanding tensile strength of 67.63 MPa. In essence, this research offers a glimpse into the nuanced factors influencing adhesive joint strength in steel. The turned, sandblasted, and plasma-treated surface emerges as a promising avenue, sparking further curiosity into the underlying mechanisms propelling superior tensile strength in adhesive joints.
ABSTRACT
The development of bonding technology and coating technologies require the use of modern materials and topologies for the demanding effect and modification of their wetting properties. For the industry, a process modification process that can be integrated into a process is the atmospheric pressure of air operation plasma surface treatment. This can be classified and evaluated based on the wettability, which has a significant impact on the adhesive force. The aim is to improve the wetting properties and to find the relationship between plasma treatment parameters, wetting, and adhesion. High Impact PolyStyrene (HIPS) was used as an experimental material, and then the plasma treatment can be treated with various adjustable parameters. The effect of plasma parameters on surface roughness, wetting contact angle, and using Fowkes theory of the surface energy have been investigated. Seven different plasma jet treatment distances were tested, combined with 5 scan speeds. Samples with the best plasma parameters were prepared from 25 mm × 25 mm overlapping adhesive joints using acrylic/cyanoacrylate. The possibility of creating a completely hydrophilic surface was achieved, where the untreated wetting edge angle decreased from 88.2° to 0° for distilled water and from 62.7° to 0° in the case of ethylene glycol. The bonding strength of High Impact PolyStyrene was increased by plasma treatment by 297%.