ABSTRACT
This work presents for the first time the possibility of reducing and tuning the work function of field emission cathodes coated with metal oxides by changing the chemical composition of oxide coatings using an example of heat-treated CNT/NiO nanocomposite structures. These cathodes are formulated using carbon nanotube (CNT) arrays that are coated with ultrathin layers of nickel oxide (CNT/NiO) by atomic layer deposition (ALD). It was found that NiO at thicknesses of several nanometers grown on CNTs heat treated at a temperature of 350 °C can change its stoichiometric composition towards the formation of oxygen vacancies, since the Ni3+/Ni2+ peak area ratio increases and the position of the Ni-O peak binding energies shifts as observed using X-ray photoelectron spectroscopy (XPS). According to the secondary electron cut-off, the work function was 4.95 for pristine CNTs and it was found that the work function of deposited NiO layers on CNTs decreased after heat treatment. The decrease in work function occurs as a result of changes in the chemical composition of the oxide film. For the heat-treated CNT/NiO composites, the work function was 4.30 eV with a NiO layer thickness of 7.6 nm, which was less than that for a NiO thin film close to the stoichiometric composition, which had a work function of 4.48 eV. The field emission current-voltage characteristics showed that the fields for producing an emission current density of 10 µA cm-2 were 5.54 V µm-1 for pure nanotubes and 4.32 V µm-1 and 4.19 V µm-1 for NiO-coated CNTs (3.8 and 7.6 nm), respectively. The present study has shown that heat treatment of deposited thin NiO layers on field cathodes is a promising approach to improve the efficiency of field emission cathodes and is a new approach in vacuum nanoelectronics that allows tuning the work function of field emission cathodes.
ABSTRACT
Laser-induced periodic surface structures (LIPSS) can be fabricated in virtually all types of solid materials and show great promise for efficient and scalable production of surface patterns with applications in various fields from photonics to engineering. While the majority of LIPSS manifest as modifications of the surface relief, in special cases, laser impact can also lead to periodic modulation of the material phase state. Here, we report on the fabrication of high-quality periodic structures in the films of phase-change material Ge2Sb2Te5 (GST). Due to considerable contrast of the refractive index of GST in its crystalline and amorphous states, the fabricated structures provide strong spatial modulation of the optical properties, which facilitates their applications. By changing the excitation laser wavelength, we observe the scaling of the grating period as well as transition between formation of different types of LIPSS. We optimize the laser exposure routine to achieve large-scale high-quality phase-change gratings with controllable period and demonstrate their reversible tunability through intermediate amorphization steps. Our results reveal the prospects of fast and rewritable fabrication of high-quality periodic structures for photonics and can serve as a guideline for further development of phase-change material-based optical elements.