ABSTRACT
The effect of the stereoregularity of poly(1-trimethylsilyl-1-propyne) [PTMSP] (cis-content from 50 to 90%) on physical aging was investigated by measurement of the gas permeability. Films from pure PTMSP as well as those with the addition of the antioxidant Irganox 1076 were exposed to the air. The permeability of pure PTMSP films increases with an increase in cis-stereoregularity and correlates with an increase in interchain distances (according to X-ray analysis). For pure PTMSP films, the most significant aging (up to 50% of permeability drop) was observed for polymers with mixed microstructure, and the slowest aging (10-30% of permeability drop) was observed for polymers with cis-regular structure. For PTMSP films with added Irganox 1076, some decrease in permeability with time is also observed. The addition of Irganox 1076 to PTMSP in mixed as well as cis-enriched configurations visibly slows down aging. In the case of cis-regular PTMSP with a slow aging rate, the introduction of an antioxidant does not provide any advantages. The high stability of cis-regular PTMSP demonstrates the possibility of obtaining more stable membrane materials with the highest equilibrium state of the polymer selective layer prepared by casting solution.
ABSTRACT
Poly-2,6-dimethylphenylene oxide (PPO) film samples with varying degrees of crystallinity (from 0 to 69%) were obtained by means of different techniques. The films were studied by various physicochemical methods (Fourier-transform infrared spectroscopy, positron annihilation lifetime spectroscopy, X-ray diffraction, and 1H nuclear magnetic resonance relaxation). Solubility coefficients of gases in the PPO samples were measured via sorption isotherms of gases by volumetric technique with chromatographic detection. The apparent activation energy of permeation and the activation energy of diffusion of all gases were estimated based on temperature dependences of gas permeability and diffusivity for amorphous and semi-crystalline PPO in the range of 20-50 °C. The peculiarities of free volume, density, and thermal properties of gas transport confirm the nanoporosity of the gas-permeable crystalline phase of PPO. So, the PPO can be included in the group of organic molecular sieves.
ABSTRACT
Changes of the spectral characteristics of absorption bands depending on the films' treatment method were registered for polyetherimide Ultem films. The possibility of selection of structural criteria (the ratio of the functional groups absorption bands intensities) showing all conformational changes in elementary unit with metrological processing of the results is shown. It is demonstrated that film formation from chloroform solution leads to elementary unit fragments, Ph-O-Ph', which have an effect on macromolecule conformation and result in increasing of space between fragments of macromolecules (local polymer matrix packing loosening). Desorption of residual chloroform from films by ethanol or supercritical CO2 leads to a change of conformers set in Im-Ph-Im' units. Quantum chemical modeling showed the possibility of convergence of these fragments in neighboring macromolecules, and consequently of interchain π-π interaction (local densification of chain packing of the polymer matrix). After annealing at a temperature higher than glass transition temperature, the polyetherimide film exhibits the most disordered (amorphous) state at all of the fragments. It is demonstrated that the results, obtained by the combination of theoretical and experimental vibrational spectroscopy methods, are in good agreement with data of chain packing ordering found by analysis of gas separation parameters.