Efficient Adsorption of Chromium Ions from Aqueous Solutions by Plant-Derived Silica.

Nowadays, there is great interest in the use of plant waste to obtain materials for environmental protection. In this study, silica powders were prepared with a simple and low-cost procedure from biomass materials such as horsetail and common reed, as well as wheat and rye straws. The starting biomass materials were leached in a boiling HCl solution. After washing and drying, the samples were incinerated at 700 °C for 1 h in air. The organic components of the samples were burned leaving final white powders. These powders were characterized by powder X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, dynamic light scattering (DLS), scanning electron microscopy (SEM), and low-temperature nitrogen sorption. The amorphous powders (biosilica) contained mainly SiO2, as indicated by FTIR analysis. Horsetail-derived silica was chosen for testing the removal of dichromate ions from water solutions. This biosilica had a good ability to adsorb Cr(VI) ions, which increased after modification of the powder with the dodecylamine surfactant. It can be concluded that the applied procedure allowed obtaining high purity biosilica from plant waste with good efficiency. The produced biosilica was helpful in removing chromium ions and showed low cytotoxicity to human endothelial cells, suggesting that it can be safely used in environmental remediation.

Aluminum Doped Titania as a Support of Copper Catalysts for SCR of Nitrogen Oxides.

Aluminum doped titania samples were synthesized as supports of copper oxide catalysts for NO reduction with ammonia. Samples were prepared by the sol-gel method with various ratios of aluminum to titanium. Their thermal stability was examined by TG/DSC methods which revealed that precursors were decomposed at 450 °C. The XRD measurements showed that aluminum caused the diminishing of titania crystallites and was built into the anatase structure or formed an amorphous phase. The admixture of aluminum in titania resulted in a significant increase in specific surface area of mesoporous supports as determined by low temperature sorption of nitrogen. Results of the catalytic tests over copper/aluminum-titania samples obtained by impregnation pointed out that the addition of aluminum broadened the temperature window of high catalytic activity. The increase in Al concentration shifted the temperature of maximum activity to higher values, and at the same time lowered nitrous oxide formation as well. Better catalytic efficiency could result from high copper dispersion on the catalysts surface, as well as the synergistic interaction between Ti and Cu causing reduction in CuO species as confirmed by XPS measurements. It was shown that copper was present as Cu+ species mainly, forming Cu-O-Ti bonds on the catalysts surface.