Bioinspired Reactive Interfaces Based on Layered Double Hydroxides-Zn Rich Hydroxyapatite with Antibacterial Activity.

This work is focused on the preparation and multi-technique characterization of potentially biocompatible reactive interfaces obtained by combining layered double hydroxides (LDHs) and hydroxyapatite (HA). Antimicrobial and osteoinductive metallic ions as Zn2+ and Ga3+ were chosen as intralayer constituents of LDH to obtain ZnAl and ZnAlGa systems. These LDHs, exchanged with dihydrogenphosphate anions, promoted the precipitation of HA on the LDH surface yielding HA@LDH composites. X-ray diffraction quantitative analysis, through the Rietveld refinement method, coupled with elemental analysis and micro-Raman spectroscopy showed the formation of a mixed Ca-Zn HA phase. Scanning electron microscopy revealed that HA, in the presence of LDH, grew preferentially along its a-axis, thus crystallizing mainly in the form of flake crystals. LDH and HA@LDH composites showed antibacterial activity against Staphylococcus aureus and Pseudomonas aeruginosa at not cytotoxic concentrations for human osteoblasts (hFob 1.19), especially when Ga cations were present in the LDH structure. The effect of the presence of HA in the composites on the bone-bonding ability and on human osteoblast proliferation was also investigated. The HA seemed to reduce the toxicity of the LDH toward human osteoblast while did not affect the bone-bonding ability. This multidisciplinary study provides the bio-chemical, structural characterization of new LDH and HA@LDH composites, evaluating also their bioactivity to be potentially applicable to titanium-based prostheses.

Use of calcium carbonate as an excipient for release of poorly water soluble drugs: The case of carbamazepine.

Carbamazepine (CBZ) is a poorly water soluble drug owing to the Biopharmaceutic Classification System (BCS) class II. It is characterized by a variable bioavailability and by the presence of different polymorphs. In this paper the effects of CaCO3 on the physicochemical properties of CBZ and its solubility and release were evaluated. CaCO3 is a naturally non-toxic biomineral and was chosen because it is a safe, cheap and eco-friendly excipient able to dissolve in an acidic environment. Composites with different CBZ loadings were prepared by ball milling and antisolvent method. The composites were characterized by X-ray powder diffraction, differential scanning calorimetry analysis and attenuated total reflectance FT-IR which revealed that both the presence of CaCO3 and the preparation procedure affect the polymorphic form crystallinity and intermolecular interactions among the drug molecules. Scanning electron microscopy showed that small drug crystals with different crystalline forms were deposited on the surface of the CaCO3 particles. Solubility and dissolution tests showed an increase in the apparent solubility of CBZ and improved drug release. These results demonstrated that CaCO3 affected the drug release properties likely due to its pH-sensitive characteristics.

Iridium-Doped Nanosized Zn-Al Layered Double Hydroxides as Efficient Water Oxidation Catalysts.

Layered double hydroxides (LDHs) are an ideal platform to host catalytic metal centers for water oxidation (WO) owing to the high accessibility of water to the interlayer region, which makes all centers potentially reachable and activated. Herein, we report the syntheses of three iridium-doped zinc-aluminum LDHs (Ir-LDHs) nanomaterials (1-3, with about 80 nm of planar size and a thickness of 8 nm as derived by field emission scanning electron microscopy and powder X-ray diffraction studies, respectively), carried out in the confined aqueous environment of reverse micelles, through a very simple and versatile procedure. These materials exhibit excellent catalytic performances in WO driven by NaIO4 at neutral pH and 25 °C, with an iridium content as low as 0.5 mol % (∼0.8 wt %), leading to quantitative oxygen yields (based on utilized NaIO4, turnover number up to ∼10,000). Nanomaterials 1-3 display the highest ever reported turnover frequency values (up to 402 min-1) for any heterogeneous and heterogenized catalyst, comparable only to those of the most efficient molecular iridium catalysts, tested under similar reaction conditions. The boost in activity can be traced to the increased surface area and pore volume (>5 times and 1 order of magnitude, respectively, higher than those of micrometric materials of size 0.3-1 µm) estimated for the nanosized particles, which guarantee higher noble metal accessibility. X-ray absorption spectroscopy (XAS) studies suggest that 1-3 nanomaterials, as-prepared and after catalysis, contain a mixture of isolated, single octahedral Ir(III) sites, with no evidence of Ir-Ir scattering from second-nearest neighbors, excluding the presence of IrO2 nanoparticles. The combination of the results obtained from XAS, elemental analysis, and ionic chromatography strongly suggests that iridium is embedded in the brucite-like structure of LDHs, having four hydroxyls and two chlorides as first neighbors. These results demonstrate that nanometric LDHs can be successfully exploited to engineer efficient WOCs, minimizing the amount of iridium used, consistent with the principle of the noble-metal atom economy.