ABSTRACT
It was shown previously that cyclic loading can be used to extend the fatigue life of sheet plastic materials subjected to the preliminary impact-oscillatory loading. This type of loading causes dynamic non-equilibrium processes (DNP) in materials, which lead to the formation of dissipative structures in materials and on their surface. The density of these dissipative structures is less than that of the base metal. In this paper, the results of investigations into the relief and hardness of surface layers modified by impact-oscillatory loading are analyzed on the example of five structural materials. The signs of a regular, orderly system of microextrusions formed on flat surfaces of all materials due to DNP are considered along with the alignment of roughness parameters Rz and Ra of relief profiles. The effect of impact-oscillatory loading is one of the main causes that lead to the extension of the fatigue life of materials.
ABSTRACT
Regularities of steel structure degradation of the "Novopskov-Aksay-Mozdok" gas main pipelines (Nevinnomysskaya CS) as well as the "Gorky-Center" pipelines (Gavrilovskaya CS) were studied. The revealed peculiarities of their degradation after long-term operation are suggested to be treated as a particular case of the damage accumulation classification (scheme) proposed by prof. H.M. Nykyforchyn. It is shown that the fracture surface consists of sections of ductile separation and localized zones of micro-spalling. The presence of the latter testifies to the hydrogen-induced embrittlement effect. However, the steels under investigation possess sufficiently high levels of the mechanical properties required for their further safe exploitation, both in terms of durability and cracking resistance.