Vacuum Low-Temperature Microwave-Assisted Pyrolysis of Technical Lignins.

Cleavage by microwave-assisted pyrolysis is a way to obtain higher-value organic chemicals from technical lignins. In this report, pine kraft lignin (PKL), spruce and beech organosolv lignin (SOSL and BOSL), and calcium lignosulfonates from spruce wood (LS) were pyrolyzed at temperatures between 30 and 280 °C using vacuum low-temperature, microwave-assisted pyrolysis. The mass balance, energy consumption, condensation rate, and pressure changes of the products during the pyrolysis process were recorded. Phenolic condensates obtained at different temperatures during pyrolysis were collected, and their chemical composition was determined by GC-MS and GC-FID. The origin of the technical lignin had a significant influence on the pyrolysis products. Phenolic condensates were obtained in yields of approximately 15% (PKL and SOSL) as well as in lower yields of 4.5% (BOSL) or even 1.7% (LS). The main production of the phenolic condensates for the PKL and SOSL occurred at temperatures of approximately 140 and 180 °C, respectively. The main components of the phenolic fraction of the three softwood lignins were guaiacol, 4-methylguaiacol, 4-ethylguaiacol, and other guaiacol derivatives; however, the quantity varied significantly depending on the lignin source. Due to the low cleavage temperature vacuum, low-temperature, microwave-assisted pyrolysis could be an interesting approach to lignin conversion.

Birch Wood Surface Characterization after Treatment with Modified Phenol-Formaldehyde Oligomers.

Phenol-formaldehyde (PF) resins with well-established molecular sizes are promising treatment agents for wood bulk protection. However, due to the presence of hydroxyl groups on the periphery, the PF oligomers tend to absorb the water, which can lead to water penetration into the wood. To overcome this drawback different PF pre-polymers have been chemically modified with different long-chain fatty acid chlorides (FAC) via esterification. To obtain the modified PF (M-PF) resins, the PF pre-polymers with average molecular weight (Mw) from 266 to 884 g/mol were esterified with decanoyl, lauroyl, myristoyl, palmitoyl, and stearoyl chloride in pyridine as the reaction medium. Silver birch (Betula pendula) wood specimens (15 × 70 × 150 mm3) were coated with M-PF pre-polymer 5% (w/w) solutions in tetrahydrofuran (THF), and hydrophobic properties of treated birch wood specimens were evaluated using surface contact angle (CA) measurements of water droplets. For all M-PF resin-treated specimens, CA was almost 2-2.5 times higher than for untreated wood (45°) and it remained 80-125° after 60 s. The aging properties of M-PF resin-coated birch wood were analyzed using artificial weathering with ultraviolet (UV) light and combination of both UV and water spray. Results clearly confirm, that the hydrophobic properties of M-PF-treated wood has short-term character and will gradually disappear during long-term application in outdoor conditions.

Preparation of Polyurethane Adhesives from Crude and Purified Liquefied Wood Sawdust.

Polyurethane (PU) adhesives were prepared with bio-polyols obtained via acid-catalyzed polyhydric alcohol liquefaction of wood sawdust and polymeric diphenylmethane diisocyanate (pMDI). Two polyols, i.e., crude and purified liquefied wood (CLW and PLW), were obtained from the liquefaction process with a high yield of 99.7%. PU adhesives, namely CLWPU and PLWPU, were then prepared by reaction of CLW or PLW with pMDI at various isocyanate to hydroxyl group (NCO:OH) molar ratios of 0.5:1, 1:1, 1.5:1, and 2:1. The chemical structure and thermal behavior of the bio-polyols and the cured PU adhesives were analyzed by Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA). Performance of the adhesives was evaluated by single-lap joint shear tests according to EN 302-1:2003, and by adhesive penetration. The highest shear strength was found at the NCO:OH molar ratio of 1.5:1 as 4.82 ± 1.01 N/mm2 and 4.80 ± 0.49 N/mm2 for CLWPU and PLWPU, respectively. The chemical structure and thermal properties of the cured CLWPU and PLWPU adhesives were considerably influenced by the NCO:OH molar ratio.

Lignin and Lignin-Derived Compounds for Wood Applications-A Review.

Improving the environmental performance of resins in wood treatment by using renewable chemicals has been a topic of interest for a long time. At the same time, lignin, the second most abundant biomass on earth, is produced in large scale as a side product and mainly used energetically. The use of lignin in wood adhesives or for wood modification has received a lot of scientific attention. Despite this, there are only few lignin-derived wood products commercially available. This review provides a summary of the research on lignin application in wood adhesives, as well as for wood modification. The research on the use of uncleaved lignin and of cleavage products of lignin is reviewed. Finally, the current state of the art of commercialization of lignin-derived wood products is presented.

Weathering Stability and Durability of Birch Plywood Modified with Different Molecular Weight Phenol-Formaldehyde Oligomers.

This study investigated the effect of phenol-formaldehyde (PF) resin treatment on the weathering stability and biological durability of birch plywood. Silver birch (Betula pendula) veneers were vacuum-pressure impregnated with four different PF resins with average molecular weights (Mw) of 292 (resin A), 528 (resin B), 703 (resin C), and 884 g/mol (resin D). The aging properties of PF resin modified birch plywood were analyzed using artificial weathering with ultraviolet (UV) light, UV and water spray, and weathering under outdoor conditions. The same combinations of PF-treated plywood specimens were then tested in soil-bed tests to determine their resistance against soft-rot wood decay. It was not possible to compare weathering processes under artificial conditions to processes under outdoor conditions. However, the weathering stability of birch plywood treated with PF resins A, B, and C, scored better than plywood treated with commercial resin D (regardless of solid content concentration [%]). Results from unsterile soil bed tests showed improvements in resistance to soft-rot wood decay compared to untreated plywood and solid wood. Mass loss [%] was lowest for birch plywood specimens treated with resin of highest solid content concentration (resin D, 20%). Provisional durability ratings delivered durability class (DC) ratings of 2-3, considerably improved over untreated solid wood and untreated birch plywood (DC 5).