ABSTRACT
Poly(ethylene oxide) (PEO) has long been used as an additive in toothpaste, partly because it reduces biofilm formation on teeth. It does not, however, reduce the formation of dental calculus or support the remineralization of dental enamel or dentine. The present article describes the synthesis of new block copolymers on the basis of PEO and poly(3-sulfopropyl methacrylate) blocks using atom transfer radical polymerization. The polymers have very large molecular weights (over 10(6) g/mol) and are highly water-soluble. They delay the precipitation of calcium phosphate from aqueous solution but, upon precipitation, lead to relatively monodisperse hydroxyapatite (HAP) spheres. Moreover, the polymers inhibit the bacterial colonization of human enamel by Streptococcus gordonii, a pioneer bacterium in oral biofilm formation, in vitro. The formation of well-defined HAP spheres suggests that a polymer-induced liquid precursor phase could be involved in the precipitation process. Moreover, the inhibition of bacterial adhesion suggests that the polymers could be utilized in caries prevention.
Subject(s)
Biofilms/drug effects , Calcium Phosphates/antagonists & inhibitors , Methacrylates/chemistry , Polyethylene Glycols/chemistry , Biofilms/growth & development , Calcium Phosphates/metabolism , Dental Enamel/drug effects , Dental Enamel/metabolism , Humans , Methacrylates/pharmacology , Polyethylene Glycols/pharmacology , Random Allocation , Saliva/drug effects , Saliva/metabolism , Streptococcus gordonii/drug effects , Streptococcus gordonii/physiology , X-Ray DiffractionABSTRACT
The polymer-controlled and bioinspired precipitation of inorganic minerals from aqueous solution at near-ambient or physiological conditions avoiding high temperatures or organic solvents is a key research area in materials science. Polymer-controlled mineralization has been studied as a model for biomineralization and for the synthesis of (bioinspired and biocompatible) hybrid materials for a virtually unlimited number of applications. Calcium phosphate mineralization is of particular interest for bone and dental repair. Numerous studies have therefore addressed the mineralization of calcium phosphate using a wide variety of low- and high-molecular-weight additives. In spite of the growing interest and increasing number of experimental and theoretical data, the mechanisms of polymer-controlled calcium phosphate mineralization are not entirely clear to date, although the field has made significant progress in the last years. A set of elegant experiments and calculations has shed light on some details of mineral formation, but it is currently not possible to preprogram a mineralization reaction to yield a desired product for a specific application. The current article therefore summarizes and discusses the influence of (macro)molecular entities such as polymers, peptides, proteins and gels on biomimetic calcium phosphate mineralization from aqueous solution. It focuses on strategies to tune the kinetics, morphologies, final dimensions and crystal phases of calcium phosphate, as well as on mechanistic considerations.
Subject(s)
Calcium Phosphates/chemistry , Minerals/chemistry , Polymers/chemistry , Water/chemistry , SolutionsABSTRACT
The self-assembly of the amphiphilic block copolymer poly(butadiene)-block-poly[2-(dimethylamino)ethyl methacrylate] at the air-water interface and the mineralization of the monolayers with calcium phosphate was investigated at different pH values. As expected for polyelectrolytes, the subphase pH strongly affects the monolayer properties. The focus of the current study, however, is on the effect of an oscillating (instead of a static) polymer monolayer on calcium phosphate mineralization. Monitoring of the surface pressure vs. mineralization time shows that the monolayer is quite stable if the mineralization is performed at pH 8. In contrast, the monolayer at pH 5 shows a measurable decrease of the surface pressure already after ca. 2 h of mineralization. Transmission electron microscopy reveals that mineralization at low pH under constant oscillation leads to small particles, which are arranged in circular features and larger entities with holes of ca. 200 nm. The larger features with the holes disappear as the mineralization is continued in favor of the smaller particles. These grow with time and form necklace-like architectures of spherical particles with a uniform diameter. In contrast, mineralization at pH 8 leads to very uniform particle morphologies already after 2 h. The mineralization products consist of a circular feature with a dark dot in the center. The increasing contrast of the precipitates in the electron micrographs with mineralization time indicates an increasing degree of mineralization vs. reaction time. The study therefore shows that mechanical effects on mineralization at interfaces are quite complex.