ABSTRACT
Stretchable electronics has received major attention in recent years due to the prospects of integrating electronics onto and into the human body. While many studies investigate how different conductive fillers perform in stretchable composites, the effect of different elastomers on composite performance, and the related fundamental understanding of what is causing the performance differences, is poorly understood. Here, we perform a systematic investigation of the elastomer influence on the electromechanical performance of gold nanowire-based stretchable conductors based on five chemically different elastomers of similar Young's modulus. The choice of elastomer has a huge impact on the electromechanical performance of the conductors under cyclic strain, as some composites perform well, while others fail rapidly at 100% strain cycling. The lack of macroscopic crack formation in the failing composites indicates that the key aspect for good electromechanical performance is not homogeneous films on the macroscale but rather beneficial interactions on the nanoscale. Based on the comprehensive characterization, we propose a failure mechanism related to the mechanical properties of the elastomers. By improving our understanding of elastomer influence on the mechanisms of electrical failure, we can move toward rational material design, which could greatly benefit the field of stretchable electronics.
ABSTRACT
Soft and stretchable nanocomposites can match the mechanical properties of neural tissue, thereby minimizing foreign body reactions to provide optimal stimulation and recording specificity. Soft materials for neural interfaces should simultaneously fulfill a wide range of requirements, including low Young's modulus (<<1 MPa), stretchability (≥30%), high conductivity (>> 1000 S cm-1), biocompatibility, and chronic stability (>> 1 year). Current nanocomposites do not fulfill the above requirements, in particular not the combination of softness and high conductivity. Here, this challenge is addressed by developing a scalable and robust synthesis route based on polymeric reducing agents for smooth, high-aspect ratio gold nanowires (AuNWs) of controllable dimensions with excellent biocompatibility. AuNW-silicone composites show outstanding performance with nerve-like softness (250 kPa), high conductivity (16 000 S cm-1), and reversible stretchability. Soft multielectrode cuffs based on the composite achieve selective functional stimulation, recordings of sensory stimuli in rat sciatic nerves, and show an accelerated lifetime stability of >3 years. The scalable synthesis method provides a chemically stable alternative to the widely used AgNWs, thereby enabling new applications within electronics, biomedical devices, and electrochemistry.
ABSTRACT
High-throughput production methods such as screen printing can bring stretchable electronics out of the lab into the market. Most stretchable conductor inks for screen printing are based on silver nanoparticles or flakes due to their favorable performance-to-cost ratio, but silver is prone to tarnishing and corrosion, thereby limiting the stability of such conductors. Here, we report on a cost-efficient and scalable approach to resolve this issue by developing screen printable inks based on silver flakes chemically coated by a thin layer of gold. The printed stretchable AgAu conductors reach a conductivity of 8500 S cm-1, remain conductive up to 250% strain, show excellent corrosion and tarnishing stability, and are used to demonstrate wearable LED and NFC circuits. The reported approach is attractive for smart clothing, as the long-term functionality of such devices is expected in a variety of environments.