Effect of Olive-Pine Bottom Ash on Properties of Geopolymers Based on Metakaolin.

In this research, the feasibility of using bottom ashes generated by the combustion of biomass (olive pruning and pine pruning) as a source of aluminosilicates (OPBA) has been studied, replacing the metakaolin precursor (MK) in different proportions (0, 25, 50, 75, and 100 wt.% substitution) for the synthesis of geopolymers. As alkaline activator an 8 M NaOH solution and a Na2SiO3 have been used. The geopolymers were cured 24 h in a climatic chamber at 60 °C in a water-saturated atmosphere, subsequently demoulded and cured at room temperature for 28 days. The results indicated that the incorporation of OPBA waste, which have 19.7 wt.% of Ca, modifies the characteristics of the products formed after alkaline activation. In general terms, the incorporation of increasing amounts of calcium-rich ashes results in geopolymers with higher bulk density. The compressive strength increases with the addition of up to 50 wt.% of OPBA with respect to the control geopolymers, contributing the composition of the residue to the acquisition of better mechanical behavior. The results indicate the potential use of these OPBA waste as raw material to produce unconventional cements with 28-day curing strengths greater than 10 MPa, and thermal conductivities less than 0.35 W/mK.

Manufacture of Sustainable Clay Bricks Using Waste from Secondary Aluminum Recycling as Raw Material.

The aluminum recycling industry produces aluminum filter dust (AFD), a waste byproduct of the aluminum recycling process composed mainly of aluminum oxide in a percentage between 60⁻70%, 8% calcium oxide, almost 15% sodium chloride, and between 5⁻10% potassium chloride. Due to its aluminum content, this waste can be used as a raw material in the manufacture of ceramic bricks, at the same time reducing the environmental impact produced in landfill. In this work, the partial substitution of a clay mixture (40% black, 30% red, and 30% yellow clay) by different proportions of AFD in the range 0⁻25 wt % for the production of fired clay brick was studied. The raw materials, clays, and waste were characterized by XRF and XRD. The brick specimens were fired at 950 °C and their physical and mechanical properties, such as water absorption, water suction, loss of ignition, linear shrinkage, bulk density, and compressive strength, were analyzed. The more relevant results were obtained with the addition of up to 20 wt % AFD, obtaining bricks with physical properties comparable to pure clay-based bricks used as a reference and better compressive strength and thermal conductivity due to the balance between the melting and pore-forming effects of the waste. These sustainable bricks also comply with the regulations of heavy metals leached to the environment, as indicated by the leaching test.