ACS Appl Mater Interfaces
; 5(16): 7726-30, 2013 Aug 28.
Article
in English
| MEDLINE
| ID: mdl-23947825
ABSTRACT
Chemical post-treatment of the carbon nanotube fiber (CNTF) was carried out via intramolecular cross-dehydrogenative coupling (ICDC) with FeCl3 at room temperature. The Raman intensity ratio of the G band to the D band (IG/ID ratio) of CNT fiber increased from 2.3 to 4.6 after ICDC reaction. From the XPS measurements, the ACâC/AC-C ratio of the CNT fiber increased from 3.6 to 4.8. It is of keen interest that both the electrical conductivity and tensile strength of CNT yarn improved to 3.5 × 10(3) S/cm and 420 MPa, which is 180 and 200% higher than that of neat CNT yarn.