Tunable Visible Light and Energy Transfer Mechanism in Tm3+ and Silver Nanoclusters within Co-Doped GeO2-PbO Glasses.

This study introduces a novel method for producing Ag nanoclusters (NCs) within GeO2-PbO glasses doped with Tm3+ ions. Sample preparation involved the melt-quenching method, employing adequate heat treatment to facilitate Ag NC formation. Absorption spectroscopy confirmed trivalent rare-earth ion incorporation. Ag NC identification and the amorphous structure were observed using transmission electron microscopy. A tunable visible emission from blue to the yellow region was observed. The energy transfer mechanism from Ag NCs to Tm3+ ions was demonstrated by enhanced 800 nm emission under 380 and 400 nm excitations, mainly for samples with a higher concentration of Ag NCs; moreover, the long lifetime decrease of Ag NCs at 600 nm (excited at 380 and 400 nm) and the lifetime increase of Tm3+ ions at 800 nm (excitation of 405 nm) corroborated the energy transfer between those species. Therefore, we attribute this energy transfer mechanism to the decay processes from S1→T1 and T1→S0 levels of Ag NCs to the 3H4 level of Tm3+ ions serving as the primary path of energy transfer in this system. GeO2-PbO glasses demonstrated potential as materials to host Ag NCs with applications for photonics as solar cell coatings, wideband light sources, and continuous-wave tunable lasers in the visible spectrum, among others.

Effect of Silver Nanoparticles on the Optical Properties of Double Line Waveguides Written by fs Laser in Nd3+-Doped GeO2-PbO Glasses.

Nd3+-doped GeO2-PbO glass with silver (Ag) nanoparticles (NPs) are produced with double line waveguides through fs laser processing for photonic applications. A Ti:sapphire fs laser at 800 nm was used to write the waveguides directly into the glass 0.7 mm beneath the surface. This platform is based on pairs of parallel lines with spacing of 10 µm, each pair being formed by two identical written lines but in two different configurations of 4 or 8 separately processed lines, which are coincident. The results of optical microscopy, absorbance measurements, refractive index change, beam quality factor (at 632 and 1064 nm), photoluminescence, propagation losses, and relative gain at 1064 nm are presented. The structural changes in the glass due to the presence of Ag NPs were investigated by Raman spectroscopy. At 632 and 1064 nm, x,y-symmetrical guiding was observed, and for both kinds of overlapping pulses, a refractive index alteration of 10-3 was found in both directions. Photoluminescence growth of ~47% at 1064 nm was observed due to the plasmonic effect of Ag NPs. In dual waveguides containing Ag NPs, the relative gain obtained increased by 40% and 30% for four and eight overlapping lines, respectively, at 600 mW of 808 nm pump power, when compared to waveguides without those metallic NPs. We highlight the resultant positive internal gains of 5.11 and 7.12 dB/cm that showed a growth of ~40% and ~30%, respectively, with respect to the samples without Ag NPs. The increase in photoluminescence and relative gain were related to the local field growth produced by Ag NPs. The present results show that the addition of Ag NPs impacts positively on the optical performance at 1064 nm of double line waveguides processed by fs laser writing in Nd3+-doped GeO2-PbO glass, opening news perspectives for photonics.