ABSTRACT
BACKGROUND: To evaluate the bleaching efficacy of at-home carbamide peroxide (CP) gels in two concentrations, containing or not a desensitizing agent. MATERIAL AND METHODS: Forty incisors were divided into four groups (n=10), according to gel concentrations (10% or 22%), and presence or not of 3% potassium nitrate in the gel. A thin layer of gel was applied to the buccal surface of each tooth for 2h/day for 4 weeks. Bleaching efficacy was measured using a spectrophotometer, and ∆E*ab, ∆E00 and ∆WID were calculated. Measurements were performed at baseline, 7, 14, 21, 28, and 35 days following the first gel application. Data were analyzed by two-way RM-ANOVA and Tukey's test (α=0.05). RESULTS: Regarding gel concentration or potassium nitrate inclusion, both gels resulted in color change above the perceptibility thresholds, which were similar between gels. Regarding time, significant differences were observed between color change values at 7 days and other time periods. ∆WID ranged from 3.8 to 9.6. Significant moderate to strong positive correlation was observed among the parameters. CONCLUSIONS: Nor the CP concentration, neither the inclusion of potassium nitrate in the gel, had influence on bleaching efficacy. All gels were effective and showed good results from the first weeks' application. Key words:Tooth bleaching, carbamide peroxide, desensitizer, potassium nitrate, color.
ABSTRACT
The objective of this study is to investigate the magnitude of structural degradation of a monolithic translucent zirconia caused by clinically relevant grinding and polishing procedures, when associated or not with low temperature degradation (LTD), induced by accelerated hydrothermal aging using autoclave or thermocycling Ninety disks (Ø12 × 1 mm) were prepared from dental zirconia for monolithic restorations (Vipi Block Zirconn Translucent, Vipi). The specimens were divided into 3 groups (n = 30) according to surface treatment: As Sintered (untreated), Grind (diamond bur), Grind + Polish (diamond bur + polish); and then subdivided according to aging method (n = 10): Baseline (no aging), Autoclave (134°C, 2.2 kgf/cm2 pressure for 5 h), and Thermocycling (200,000 cycles, 5°C and 55°C, for 15 s each). Roughness, biaxial flexural strength and percentage of monoclinic phase were evaluated. Regarding surface treatment, the Grind group presented higher roughness and greater flexural strength compared to As Sintered group, while Grind + Polish showed intermediate roughness and flexural strength similar to Grind group. Aging had little effect on roughness, but yielded a significant reduction in flexural strength. Tetragonal to monoclinic phase transformation was observed in all groups, caused by both mechanical stresses (grinding and polishing) and LTD, which was similarly induced by the traditional autoclave method, as well as the thermocycling method The use of diamond burs to grind zirconia surface may result in deleterious effects on the surface quality of monolithic zirconia restorations, yet has a potential toughening effect by phase transformation. However, when zirconia is exposed to LTD, regardless of the surface treatment, degradation of the surface quality and strength are observed.