ABSTRACT
The paper presents the synthesis and characterization of new cobalt ferrite-lignin hybrids. The hybrids were obtained through the combustion of cobalt nitrate and ferric nitrate, two kinds of lignin being used as combustion agents. The temperatures of calcination were 500 °C and 900 °C, respectively. The hybrids were characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray powder diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray (EDX), and X-ray photoelectron spectroscopy (XPS). The magnetic properties were also assessed by vibrating sample magnetometer system (VSM). This facile synthesis method made it possible to obtain cobalt ferrite-lignin hybrids with a spinel structure. Their particle sizes and crystallite sizes have increased with an increment in the calcination temperature. A different occupancy of cations at octahedral and tetrahedral sites also occurred upon the increase in temperature. The hybrids comprising organic lignin presented the best magnetic properties.
ABSTRACT
Novel hybrid inorganic CoFe2O4/carboxymethyl cellulose (CMC) polymeric framework nanobeads-type adsorbents with tailored magnetic properties were synthesized by a combination of coprecipitation and flash-cooling technology. Precise self-assembly engineering of their shape and composition combined with deep testing for cadmium removal from wastewater are investigated. The development of a single nanoscale object with controllable composition and spatial arrangement of CoFe2O4 (CF) nanoparticles in carboxymethyl cellulose (CMC) as polymeric matrix, is giving new boosts to treatments of wastewaters containing heavy metals. The magnetic nanobeads were characterized by means of scanning electron microscopy (SEM), powder X-ray diffraction analysis (XRD), thermogravimetric analysis (TG), and vibrational sample magnetometer (VSM). The magnetic properties of CF@CMC sample clearly exhibit ferromagnetic nature. Value of 40.6 emu/g of saturation magnetization would be exploited for magnetic separation from aqueous solution. In the adsorptions experiments the assessment of equilibrium and kinetic parameters were carried out by varying adsorbent dosage, contact time and cadmium ion concentration. The kinetic behavior of adsorption process was best described by pseudo-second-order model and the Langmuir isotherm was fitted best with maximum capacity uptake of 44.05 mg/g.
ABSTRACT
In this research, we reported on the formation of highly porous foam SrTiO3/NiFe2O4 (100-xSTO/xNFO) heterostructure by joint solid-state and sol-gel auto-combustion techniques. The colloidal assembly process is discussed based on the weight ratio x (x = 0, 25, 50, 75, and 100 wt %) of NiFe2O4 in the 100-xSTO/xNFO system. We proposed a mechanism describing the highly porous framework formation involving the self-assembly of SrTiO3 due to the gelation process of the nickel ferrite. We used a series of spectrophotometric techniques, including powder X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), N2 adsorption isotherms method, UV-visible diffuse reflectance spectra (UV-Vis DRS), vibrating sample magnetometer (VSM), and dielectric measurements, to investigate the structural, morphological, optical, magnetic, and dielectric properties of the synthesized samples. As revealed by FE-SEM analysis and textural characteristics, SrTiO3-NiFe2O4 nanocomposite self-assembled into a porous foam with an internally well-defined porous structure. HRTEM characterization certifies the distinctive crystalline phases obtained and reveals that SrTiO3 and NiFe2O4 nanoparticles were closely connected. The specific magnetization, coercivity, and permittivity values are higher in the 75STO/25NFO heterostructure and do not decrease proportionally to the amount of non-magnetic SrTiO3 present in the composition of samples.