ABSTRACT
Lead-free piezoelectric powders (K0.44Na0.52Li0.04)(Nb0.82Ta0.10Sb0.04)O3 were obtained by conventional and microwave-assisted reactive heating. Firstly, the synthesis of the material was carried out following the mixed oxide route and employing both traditional methods and microwave technology. Thermogravimetry, X-ray diffraction, field emission scanning electron microscopy and electrical properties analyses were evaluated. X-ray diffraction of the powders calcined by the microwave process shows the formation of perovskite structure with orthorhombic geometry, but it is possible to observe the presence of other phases. The presence of the secondary phases found can have a great influence on the heating rate during the synthesis on which the kinetics of the reaction of formation of the piezoelectric compound depend. The calcined powder was sintered at different temperatures by conventional and non-conventional processes. The microstructure of the ceramics sintered by microwave at 1050 °C for 10 min shows perovskite cubes with regular geometry, of size close to 2-5 µm. However, the observed porosity (~8%), the presence of liquid phase and secondary phases in the microstructure of the microwave sintered materials lead to a decrease of the piezoelectric constant. The highest d33 value of 146 pC/N was obtained for samples obtained by conventional at 1100 °C 2 h compared to samples sintered by microwave at 1050 °C 10 min (~15 pC/N).
ABSTRACT
The choice of the right material is essential in microwave processing. The carbon materials are good microwave absorbers, which allows them to be transformed by microwave heating into new carbon materials with adapted properties, capable of heating other materials indirectly. In this paper, the microwave heating of graphene as reinforcement of the lithium aluminosilicate (LAS) ceramics has been explored. LAS ceramics have a near-zero coefficient of thermal expansion and exhibit an effective and efficient heating by microwave. Nevertheless, we have found that the graphene did not show any significant response to the microwave radiation and, hence, the interaction as mechanical reinforcement with the LAS material is harmful. The possible benefits of graphene materials to microwave technology are widely known; however, the mechanism involved in the interaction of microwave radiation with ceramic-graphene composites with high dielectric loss factors has not been addressed earlier.
ABSTRACT
Materials with a very low or tailored thermal expansion have many applications ranging from cookware to the aerospace industry. Among others, lithium aluminosilicates (LAS) are the most studied family with low and negative thermal expansion coefficients. However, LAS materials are electrical insulators and have poor mechanical properties. Nanocomposites using LAS as a matrix are promising in many applications where special properties are achieved by the addition of one or two more phases. The main scope of this work is to study the sinterability of carbon nanofiber (CNFs)/LAS and CNFs/alumina/LAS nanocomposites, and to adjust the ratio among components for obtaining a near-zero or tailored thermal expansion. Spark plasma sintering of nanocomposites, consisting of commercial CNFs and alumina powders and an ad hoc synthesized ß-eucryptite phase, is proposed as a solution to improving mechanical and electrical properties compared with the LAS ceramics obtained under the same conditions. X-ray diffraction results on phase compositions and microstructure are discussed together with dilatometry data obtained in a wide temperature range (-150 to 450 °C). The use of a ceramic LAS phase makes it possible to design a nanocomposite with a very low or tailored thermal expansion coefficient and exceptional electrical and mechanical properties.