ABSTRACT
High-temperature superconductors (HTS) could enable high-field magnets stronger than is possible with Nb-Ti and Nb3Sn, but two challenges have so far been the low engineering critical current density JE, especially in high-current cables, and the danger of quenches. Most HTS magnets made so far have been made out of REBCO coated conductor. Here we demonstrate stable, reliable and training-quench-free performance of Bi-2212 racetrack coils wound with a Rutherford cable fabricated from wires made with a new precursor powder. These round multifilamentary wires exhibited a record JE up to 950 A/mm2 at 30 T at 4.2 K. These coils carried up to 8.6 kA while generating 3.5 T at 4.2 K at a JE of 1020 A/mm2. Different from the unpredictable training performance of Nb-Ti and Nb3Sn magnets, these Bi-2212 magnets showed no training quenches and entered the flux flow state in a stable manner before thermal runaway and quench occurred. Also different from Nb-Ti, Nb3Sn, and REBCO magnets for which localized thermal runaways occur at unpredictable locations, the quenches of Bi-2212 magnets consistently occurred in the high field regions over a long conductor length. These characteristics make quench detection simple, enabling safe protection, and suggest a new paradigm of constructing quench-predictable superconducting magnets from Bi-2212.
ABSTRACT
Superconducting joints are one of the key components needed to make Ag-alloy clad Bi2Sr2CaCu2O8+x (Bi-2212) superconducting round wire (RW) successful for high-field, high-homogeneity magnet applications, especially for nuclear magnetic resonance (NMR) magnets in which persistent current mode (PCM) operation is highly desired. In this study, a procedure for fabricating superconducting joints between Bi-2212 round wires during coil reaction was developed. Melting temperatures of Bi-2212 powder with different amounts of Ag addition were investigated by differential thermal analysis (DTA) so as to provide information for selecting the proper joint matrix. Test joints of 1.3 mm dia. wires heat treated in 1 bar flowing oxygen using the typical partial melt Bi-2212 heat treatment (HT) had transport critical currents I c of ~900 A at 4.2 K and self-field, decreasing to ~480 A at 14 T evaluated at 0.1 µV/cm at 4.2 K. Compared to the I c of the open-ended short conductor samples with identical 1 bar HT, the I c values of the superconducting joint are ~20% smaller than that of conductor samples measured in parallel field but ~20% larger than conductor samples measured in perpendicular field. Microstructures examined by scanning electron microscopy (SEM) clearly showed the formation of a superconducting Bi-2212 interface between the two Bi-2212 round wires. Furthermore, a Bi-2212 RW closed-loop solenoid with a superconducting joint heat treated in 1 bar flowing oxygen showed an estimated joint resistance below 5×10-12 Ω based on its field decay rate. This value is sufficiently low to demonstrate the potential for persistent operation of large inductance Bi-2212 coils.