Triboemission of hydrocarbon molecules from diamond-like carbon friction interface induces atomic-scale wear.

Understanding atomic-scale wear is crucial to avoid device failure. Atomic-scale wear differs from macroscale wear because chemical reactions and interactions at the friction interface are dominant in atomic-scale tribological behaviors, instead of macroscale properties, such as material strength and hardness. It is particularly challenging to reveal interfacial reactions and atomic-scale wear mechanisms. Here, our operando friction experiments with hydrogenated diamond-like carbon (DLC) in vacuum demonstrate the triboemission of various hydrocarbon molecules from the DLC friction interface, indicating its atomic-scale chemical wear. Furthermore, our reactive molecular dynamics simulations reveal that this triboemission of hydrocarbon molecules induces the atomic-scale mechanical wear of DLC. As the hydrogen concentration in hydrogenated DLC increases, the chemical wear increases while mechanical wear decreases, indicating an opposite effect of hydrogen concentration on chemical and mechanical wear. Consequently, the total wear shows a concave hydrogen concentration dependence, with an optimal hydrogen concentration for wear reduction of around 20%.

Superlubricity of glycerol by self-sustained chemical polishing.

An impressive superlow coefficient of friction (CoF) as low as 0.004 (nearly equivalent to the rolling coefficient) was obtained by sliding a steel ball against a tetrahedral amorphous diamond-like carbon (ta-C) coating in glycerol under a boundary lubrication regime. X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM) revealed substantial changes in the surface chemistry and topography in the friction track. As shown by XPS analysis, a transfer of iron atoms from the steel ball to the ta-C layer occurred, forming iron oxy-hydroxide (FeOOH) termination on both surfaces. Between them, theoretical calculations show that a nanometre-thick fluid film consisting of glycerol and its degradation products prevents direct contact between the solid surfaces by nm-thick film EHL lubrication and results in the superlow friction, in agreement with the experiment. Furthermore, molecular dynamics (MD) simulations reveal that hydrogen atoms act as "low-friction brushes" between sliding layers of crystalline FeOOH, resulting also in low friction. A new model of sustainable green superlubricity is proposed. The tribo-formation of FeOOH with glycerol leads to a unique polishing process, which in turn leads to a self-sustained Elasto-Hydrodynamic Lubrication (EHL) regime until the very thin fluid film is no more than a few nanometres thick. At lower thicknesses, the hydroxide layer takes over. Wear of the ta-C coating is negligible, while wear on the steel ball is very moderate and acceptable for many practical applications, such as bio-tribology and the food industry, in which green lubrication is especially needed.