ABSTRACT
The well-defined silica-supported molybdenum oxo alkyl species (≡SiO-)MoO(CH2tBu)3 was selectively prepared by grafting of MoO(CH2tBu)3Cl onto partially dehydroxylated silica (silica700) using the surface organometallic chemistry approach. This surface species was fully characterized by elemental analysis and DRIFT, solid-state NMR, and EXAFS spectroscopy. This new material is related to the active species of industrial supported MoO3/SiO2 olefin metathesis catalysts. It displays very high activity in propene self-metathesis at mild (turnover number = 90â¯000 after 25 h). Remarkably, its catalytic performance outpaces those of the parent imido derivative and its tungsten oxo analogue.
ABSTRACT
Ring opening metathesis polymerization (ROMP) of bicyclo[2.2.1]hept-2-ene (norbornene) is carried out over silica-supported catalysts based on tungsten complexes bearing an oxo ligand (1: [(SiO)W(O)(CH2 SiMe3 )3 , 2: [(SiO)W(O)(CHCMe2 Ph)(dAdPO)], dAdPO  2,6 diadamantyl-4-methylphenoxide, 3: [(SiO)2 W(O)(CH2 SiMe3 )2 ]). The evaluation of the catalytic activities of the aforementioned materials in ROMP indicates that at low reaction time (0.5 min), the highest polymer yield is obtained with catalyst 2. However, for longer reaction time (>2 min), complex 3, a model of the industrial catalyst, exhibits a better monomer conversion. The polymers obtained are characterized. Moreover, these catalysts are shown to be rather preferentially selective to give the cis polynorbornene (>65%), characterized by high melting points (≈300 °C). The experimental values of the average molecular weight (Mn ) of polynorbornenes are found to be close to the theoretical ones for the polymers prepared using catalyst 2 and higher for those originated from catalyst 3.
ABSTRACT
The grafting of an oxo chloro trisalkyl tungsten derivative on silica dehydroxylated at 700 °C was studied by several techniques that showed reaction via W-Cl cleavage, to afford a well-defined precatalyst for alkene metathesis. This was further confirmed by DFT calculations on the grafting process. (17)O labeling of the oxo moiety of a series of related molecular and supported tungsten oxo derivatives was achieved, and the corresponding (17)O MAS NMR spectra were recorded. Combined experimental and theoretical NMR studies yielded information on the local structure of the surface species. Assessment of the (17)O NMR parameters also confirmed the nature of the grafting pathway by ruling out other possible grafting schemes, thanks to highly characteristic anisotropic features arising from the quadrupolar and chemical shift interactions.