ABSTRACT
PURPOSE: The aim of this study was to appraise the some mechanical properties of polymethyl methacrylate based denture base resin polymerized by copolymerization mechanism, and to investigate the cytotoxic effect of these copolymer resins. MATERIALS AND METHODS: 2-hydroxyethyl methacrylate (HEMA) and isobutyl methacrylate (IBMA) were added to monomers of conventional heat polymerized and injection-molded poly methyl methacrylate (PMMA) resin contents of 2%, 3%, and 5% by volume and polymerization was carried out. Three-point bending test was performed to detect flexural strength and the elasticity modulus of the resins. To determine the statistical differences between the study groups, the Kruskall-Wallis test was performed. Then pairwise comparisons were performed between significant groups by Mann-Whitney U test. Agar-overlay test was performed to determine cytotoxic effect of copolymer resins. Chemical analysis was determined by FTIR spectrum. RESULTS: Synthesis of the copolymer was approved by FTIR spectroscopy. Within the conventional heat-polymerized group maximum transverse strength had been seen in the HEMA 2% concentration; however, when the concentration ratio increased, the strength decreased. In the injection-molded group, maximum transverse strength had been seen in the IBMA 2% concentration; also as the concentration ratio increased, the strength decreased. Only IBMA showed no cytotoxic effect at low concentrations when both two polymerization methods applied while HEMA showed cytotoxic effect in the injection-molded resins. CONCLUSION: Within the limitations of this study, it may be concluded that IBMA and HEMA may be used in low concentration and at high temperature to obtain non-cytotoxic and durable copolymer structure.
ABSTRACT
PURPOSE: This in vitro study intended to investigate the mechanical and thermal characteristics of Valplast, and of polymethyl methacrylate denture base resin in which different esthetic fibers (E-glass, nylon 6 or nylon 6.6) were added. MATERIALS AND METHODS: FIVE GROUPS WERE FORMED: control (PMMA), PMMA-E glass, PMMA-nylon 6, PMMA-nylon 6.6 and Valplast resin. For the transverse strength test the specimens were prepared in accordance with ANSI/ADA specification No.12, and for the impact test ASTM D-256 standard were used. With the intent to evaluate the properties of transverse strength, the three-point bending (n=7) test instrument (Lloyd NK5, Lloyd Instruments Ltd, Fareham Hampshire, UK) was used at 5 mm/min. A Dynatup 9250 HV (Instron, UK) device was employed for the impact strength (n=7). All of the resin samples were tested by using thermo-mechanical analysis (Shimadzu TMA 50, Shimadzu, Japan). The data were analyzed by Kruskal-Wallis and Tukey tests for pairwise comparisons of the groups at the 0.05 level of significance. RESULTS: IN ALL MECHANICAL TESTS, THE HIGHEST VALUES WERE OBSERVED IN VALPLAST GROUP (TRANSVERSE STRENGTH: 117.22 ± 37.80 MPa, maximum deflection: 27.55 ± 1.48 mm, impact strength: 0.76 ± 0.03 kN). Upon examining the thermo-mechanical analysis data, it was seen that the E value of the control sample was 8.08 MPa, higher than that of the all other samples. CONCLUSION: Although Valplast denture material has good mechanical strength, its elastic modulus is not high enough to meet the standard of PMMA materials.
ABSTRACT
This study was conducted to observe the changes in impact resistance of a denture base resin reinforced with five types of fiber. E-glass, polyester, rayon, nylon 6, and nylon 6/6 fibers were cut into 2, 4, and 6 mm lengths and added into the resin at a concentration of 3% by weight. Five test specimens for each formulation, as well as control specimens without fiber, were prepared using a mold including a V-shaped notch with 55 x 10 x10 mm dimensions. Impact tests were carried out using a Charpy-type tester. Additionally, surfaces of the impact sections were observed under a scanning electron microscope (SEM). Results indicated that impact energy tended to increase with fiber length, and that the highest value was recorded for rayon fiber-reinforced specimens of 6 mm length. E-glass fiber reinforcement produced relatively stable, high values for each length, whereby good interfacial strength between polymer matrix and glass fibers was confirmed by SEM analysis.