ABSTRACT
Today, Ni-Cr steel is used for advanced applications in the high-temperature and electrical industries, medical equipment, food industry, agriculture and is applied in food and beverage packaging and kitchenware, automotive or mesh. A study of input steel powder from various stages of the recycling process intended for 3D printing was conducted. In addition to the precise evaluation of the morphology, particle size and composition of the powders used for laser 3D printing, special testing and evaluation of the heat-treated powders were carried out. Heat treatment up to 950 °C in an air atmosphere revealed the properties of powders that can appear during laser sintering. The powders in the oxidizing atmosphere change the phase composition and the original FeNiCr stainless steel changes to a two-phase system of Fe3Ni and Cr2O3, as evaluated by X-ray diffraction analysis. Observation of the morphology showed the separation of the oxidic phase in the sense of a brittle shell. The inner part of the powder particle is a porous compact core. The particle size is generally reduced due to the peeling of the oxide shell. This effect can be critical to 3D printing processing, causing defects on the printed parts, as well as reducing the usability of the precursor powder and can also change the properties of the printed part.
ABSTRACT
The paper presented the findings obtained by industrial research and experimental development on the use of rare earth metals (REMs) in the production of heavy steel ingots and their impact on the internal quality of the 42CrMo4 grade steel forging. REMs alloying was carried out after vacuuming the steel. A relatively large melting loss of cerium (about 50%) and its further decrease in casting due to reoxidation were observed. Refinement of structure and better mechanical properties of forged bar containing about 0.02 wt.% of Ce compared to that of the standard production were not achieved. The wind power shaft with content of about 0.06 wt.% of Ce showed high amount of REM inclusions, which were locally chained, and in some cases, initiated cracks. Four stoichiometrically different types of REM inclusions were detected in forgings, namely (La-Ce)2O2S + (La-Ce)O2 + SiO2 (minority); oxygen, phosphorus, arsenic, and antimony bound to lanthanum and cerium probably bonded with iron oxides La + Ce, MgO, Al2O3 a SiO2; (La-Ce)2O2S, FeO, SiO2, and CaO or CaS.
ABSTRACT
The polyamide (PA)-12 material used for additive manufacturing was studied in aspects of morphology and their structural properties for basic stages received during 3D laser printing. Samples were real, big-scale production powders. The structure of polymer was evaluated from the crystallinity point of view using XRD, FTIR, and DSC methods and from the surface properties using specific surface evaluation and porosity. Scanning electron microscopy was used to observe morphology of the surface and evaluate the particle size and shape via image analysis. Results were confronted with laser diffraction particles size measurement along with an evaluation of the specific surface area. Fresh PA12 powder was found as inhomogeneous in particle size of material with defective particles, relatively high specific surface, high lamellar crystallite size, and low crystallinity. The scrap PA12 crystallinity was about 2% higher than values for fresh PA12 powder. Particles had a very low, below 1 m2/g, specific surface area; particles sintered as twin particles and often in polyhedral shapes.