Achieving Planar Zn Electroplating in Aqueous Zinc Batteries with Cathode-Compatible Current Densities by Cycling under Pressure.

The value of aqueous zinc-ion rechargeable batteries is held back by the degradation of the Zn metal anode with repeated cycling. While raising the operating current density is shown to alleviate this anode degradation, such high cycling rates are not compatible with full cells, as they cause Zn-host cathodes to undergo capacity decay. A simple approach that improves anode performance while using more modest cathode-compatible current densities is required. This work reports reversible planar Zn deposition under cathode-compatible current densities can instead be achieved by applying external pressure to the cell. Employing multiscale characterization, this work illustrates how cycling under pressure results in denser and more uniform Zn deposition, analogous to that achieved under high cycling rates, even at low areal current densities of 1 to 10 mA cm-2. Microstructural mechanical measurements reveal that Zn structures plated under lower current densities are particularly susceptible to pressure-induced compression. The ability to achieve planar Zn plating at cathode-compatible current densities holds significant promise for enabling high-capacity Zn-ion battery full cells.

Lithium Borate Polycarbonates for High-Capacity Solid-State Composite Cathodes.

Improving composite cathode function is key to the success of the solid-state battery. Maximizing attainable cathode capacity and retention requires integrating suitable polymeric binders that retain a sufficiently high ionic conductivity and long-term chemo-mechanical stability of the cathode active material-solid-electrolyte-carbon mixture. Herein, we report block copolymer networks composed of lithium borate polycarbonates and poly(ethylene oxide) that improved the capacity (200 mA h g-1 at 1.75 mA cm-2) and capacity retention (94% over 300 cycles) of all-solid-state composite cathodes with nickel-rich LiNi0.8Co0.1Mn0.1O2 cathode active material, Li6PS5Cl solid electrolyte, and carbon. Tetrahedral B(OR)2(OH)2- anions immobilized on the polycarbonate segments provide hydrogen-bonding chain crosslinking and selective Li-counterion conductivity, parameterized by Li-ion transference numbers close to unity (tLi+ ~ 0.94). With 90 wt% polycarbonate content and a flexible low glass transition temperature backbone, the single-ion conductors achieved high Li-ion conductivities of 0.2 mS cm-1 at 30°C. The work should inform future binder design for improving the processability of cathode composites towards commercialising solid-state batteries, and allow use in other cell configurations, such as lithium-sulphur cathode designs.

Trapped O2 and the origin of voltage fade in layered Li-rich cathodes.

Oxygen redox cathodes, such as Li1.2Ni0.13Co0.13Mn0.54O2, deliver higher energy densities than those based on transition metal redox alone. However, they commonly exhibit voltage fade, a gradually diminishing discharge voltage on extended cycling. Recent research has shown that, on the first charge, oxidation of O2- ions forms O2 molecules trapped in nano-sized voids within the structure, which can be fully reduced to O2- on the subsequent discharge. Here we show that the loss of O-redox capacity on cycling and therefore voltage fade arises from a combination of a reduction in the reversibility of the O2-/O2 redox process and O2 loss. The closed voids that trap O2 grow on cycling, rendering more of the trapped O2 electrochemically inactive. The size and density of voids leads to cracking of the particles and open voids at the surfaces, releasing O2. Our findings implicate the thermodynamic driving force to form O2 as the root cause of transition metal migration, void formation and consequently voltage fade in Li-rich cathodes.

Alternatives to fluorinated binders: recyclable copolyester/carbonate electrolytes for high-capacity solid composite cathodes.

Optimising the composite cathode for next-generation, safe solid-state batteries with inorganic solid electrolytes remains a key challenge towards commercialisation and cell performance. Tackling this issue requires the design of suitable polymer binders for electrode processability and long-term solid-solid interfacial stability. Here, block-polyester/carbonates are systematically designed as Li-ion conducting, high-voltage stable binders for cathode composites comprising of single-crystal LiNi0.8Mn0.1Co0.1O2 cathodes, Li6PS5Cl solid electrolyte and carbon nanofibres. Compared to traditional fluorinated polymer binders, improved discharge capacities (186 mA h g-1) and capacity retention (96.7% over 200 cycles) are achieved. The nature of the new binder electrolytes also enables its separation and complete recycling after use. ABA- and AB-polymeric architectures are compared where the A-blocks are mechanical modifiers, and the B-block facilitates Li-ion transport. This reveals that the conductivity and mechanical properties of the ABA-type are more suited for binder application. Further, catalysed switching between CO2/epoxide A-polycarbonate (PC) synthesis and B-poly(carbonate-r-ester) formation employing caprolactone (CL) and trimethylene carbonate (TMC) identifies an optimal molar mass (50 kg mol-1) and composition (wPC 0.35). This polymer electrolyte binder shows impressive oxidative stability (5.2 V), suitable ionic conductivity (2.2 × 10-4 S cm-1 at 60 °C), and compliant viscoelastic properties for fabrication into high-performance solid composite cathodes. This work presents an attractive route to optimising polymer binder properties using controlled polymerisation strategies combining cyclic monomer (CL, TMC) ring-opening polymerisation and epoxide/CO2 ring-opening copolymerisation. It should also prompt further examination of polycarbonate/ester-based materials with today's most relevant yet demanding high-voltage cathodes and sensitive sulfide-based solid electrolytes.

Diagnosing the Electrostatic Shielding Mechanism for Dendrite Suppression in Aqueous Zinc Batteries.

Aqueous zinc electrolytes offer the potential for cheaper rechargeable batteries due to their safe compatibility with the high capacity metal anode; yet, they are stymied by irregular zinc deposition and consequent dendrite growth. Suppressing dendrite formation by tailoring the electrolyte is a proven approach from lithium batteries; yet, the underlying mechanistic understanding that guides such tailoring does not necessarily directly translate from one system to the other. Here, it is shown that the electrostatic shielding mechanism, a fundamental concept in electrolyte engineering for stable metal anodes, has different consequences for the plating morphology in aqueous zinc batteries. Operando electrochemical transmission electron microscopy is used to directly observe the zinc nucleation and growth under different electrolyte compositions and reveal that electrostatic shielding additive suppresses dendrites by inhibiting secondary zinc nucleation along the (100) edges of existing primary deposits and encouraging preferential deposition on the (002) faces, leading to a dense and block-like zinc morphology. The strong influence of the crystallography of Zn on the electrostatic shielding mechanism is further confirmed with Zn||Ti cells and density functional theory modeling. This work demonstrates the importance of considering the unique aspects of the aqueous zinc battery system when using concepts from other battery chemistries.

The accumulation of Li2CO3 in a Li-O2 battery with dual mediators.

One of the most important challenges facing long cycle life Li-O2 batteries is solvent degradation. Even the most stable ethers, such as CH3O(CH2CH2O)CH3, degrade to form products including Li2CO3, which accumulates in the pores of the gas diffusion electrode on cycling leading to polarisation and capacity fading. In this work, we examine the build-up and distribution of Li2CO3 within the porous gas diffusion electrode during cycling and its link to the cell failure. We also demonstrate that the removal of Li2CO3 by a redox mediator can partially recover the cell performance and extend the cycle life of a Li-O2 battery.

High-energy all-solid-state lithium batteries enabled by Co-free LiNiO2 cathodes with robust outside-in structures.

A critical current challenge in the development of all-solid-state lithium batteries (ASSLBs) is reducing the cost of fabrication without compromising the performance. Here we report a sulfide ASSLB based on a high-energy, Co-free LiNiO2 cathode with a robust outside-in structure. This promising cathode is enabled by the high-pressure O2 synthesis and subsequent atomic layer deposition of a unique ultrathin LixAlyZnzOδ protective layer comprising a LixAlyZnzOδ surface coating region and an Al and Zn near-surface doping region. This high-quality artificial interphase enhances the structural stability and interfacial dynamics of the cathode as it mitigates the contact loss and continuous side reactions at the cathode/solid electrolyte interface. As a result, our ASSLBs exhibit a high areal capacity (4.65 mAh cm-2), a high specific cathode capacity (203 mAh g-1), superior cycling stability (92% capacity retention after 200 cycles) and a good rate capability (93 mAh g-1 at 2C). This work also offers mechanistic insights into how to break through the limitation of using expensive cathodes (for example, Co-based) and coatings (for example, Nb-, Ta-, La- or Zr-based) while still achieving a high-energy ASSLB performance.

A lithium-air battery and gas handling system demonstrator.

The lithium-air (Li-air) battery offers one of the highest practical specific energy densities of any battery system at >400 W h kgsystem-1. The practical cell is expected to operate in air, which is flowed into the positive porous electrode where it forms Li2O2 on discharge and is released as O2 on charge. The presence of CO2 and H2O in the gas stream leads to the formation of oxidatively robust side products, Li2CO3 and LiOH, respectively. Thus, a gas handling system is needed to control the flow and remove CO2 and H2O from the gas supply. Here we present the first example of an integrated Li-air battery with in-line gas handling, that allows control over the flow and composition of the gas supplied to a Li-air cell and simultaneous evaluation of the cell and scrubber performance. Our findings reveal that O2 flow can drastically impact the capacity of cells and confirm the need for redox mediators. However, we show that current air-electrode designs translated from fuel cell technology are not suitable for Li-air cells as they result in the need for higher gas flow rates than required theoretically. This puts the scrubber under a high load and increases the requirements for solvent saturation and recapture. Our results clarify the challenges that must be addressed to realise a practical Li-air system and will provide vital insight for future modelling and cell development.

Dendrite initiation and propagation in lithium metal solid-state batteries.

All-solid-state batteries with a Li anode and ceramic electrolyte have the potential to deliver a step change in performance compared with today's Li-ion batteries1,2. However, Li dendrites (filaments) form on charging at practical rates and penetrate the ceramic electrolyte, leading to short circuit and cell failure3,4. Previous models of dendrite penetration have generally focused on a single process for dendrite initiation and propagation, with Li driving the crack at its tip5-9. Here we show that initiation and propagation are separate processes. Initiation arises from Li deposition into subsurface pores, by means of microcracks that connect the pores to the surface. Once filled, further charging builds pressure in the pores owing to the slow extrusion of Li (viscoplastic flow) back to the surface, leading to cracking. By contrast, dendrite propagation occurs by wedge opening, with Li driving the dry crack from the rear, not the tip. Whereas initiation is determined by the local (microscopic) fracture strength at the grain boundaries, the pore size, pore population density and current density, propagation depends on the (macroscopic) fracture toughness of the ceramic, the length of the Li dendrite (filament) that partially occupies the dry crack, current density, stack pressure and the charge capacity accessed during each cycle. Lower stack pressures suppress propagation, markedly extending the number of cycles before short circuit in cells in which dendrites have initiated.

Why charging Li-air batteries with current low-voltage mediators is slow and singlet oxygen does not explain degradation.

Although Li-air rechargeable batteries offer higher energy densities than lithium-ion batteries, the insulating Li2O2 formed during discharge hinders rapid, efficient re-charging. Redox mediators are used to facilitate Li2O2 oxidation; however, fast kinetics at a low charging voltage are necessary for practical applications and are yet to be achieved. We investigate the mechanism of Li2O2 oxidation by redox mediators. The rate-limiting step is the outer-sphere one-electron oxidation of Li2O2 to LiO2, which follows Marcus theory. The second step is dominated by LiO2 disproportionation, forming mostly triplet-state O2. The yield of singlet-state O2 depends on the redox potential of the mediator in a way that does not correlate with electrolyte degradation, in contrast to earlier views. Our mechanistic understanding explains why current low-voltage mediators (<+3.3 V) fail to deliver high rates (the maximum rate is at +3.74 V) and suggests important mediator design strategies to deliver sufficiently high rates for fast charging at potentials closer to the thermodynamic potential of Li2O2 oxidation (+2.96 V).

Batteries for wearables.

This perspective article highlights the recent advances and future challenges of battery technologies for wearables.

Transition metal migration and O2 formation underpin voltage hysteresis in oxygen-redox disordered rocksalt cathodes.

Lithium-rich disordered rocksalt cathodes display high capacities arising from redox chemistry on both transition-metal ions (TM-redox) and oxygen ions (O-redox), making them promising candidates for next-generation lithium-ion batteries. However, the atomic-scale mechanisms governing O-redox behaviour in disordered structures are not fully understood. Here we show that, at high states of charge in the disordered rocksalt Li2MnO2F, transition metal migration is necessary for the formation of molecular O2 trapped in the bulk. Density functional theory calculations reveal that O2 is thermodynamically favoured over other oxidised O species, which is confirmed by resonant inelastic X-ray scattering data showing only O2 forms. When O-redox involves irreversible Mn migration, this mechanism results in a path-dependent voltage hysteresis between charge and discharge, commensurate with the hysteresis observed electrochemically. The implications are that irreversible transition metal migration should be suppressed to reduce the voltage hysteresis that afflicts O-redox disordered rocksalt cathodes.

Buffering Volume Change in Solid-State Battery Composite Cathodes with CO2-Derived Block Polycarbonate Ethers.

Polymers designed with a specific combination of electrochemical, mechanical, and chemical properties could help overcome challenges limiting practical all-solid-state batteries for high-performance next-generation energy storage devices. In composite cathodes, comprising active cathode material, inorganic solid electrolyte, and carbon, battery longevity is limited by active particle volume changes occurring on charge/discharge. To overcome this, impractical high pressures are applied to maintain interfacial contact. Herein, block polymers designed to address these issues combine ionic conductivity, electrochemical stability, and suitable elastomeric mechanical properties, including adhesion. The block polymers have "hard-soft-hard", ABA, block structures, where the soft "B" block is poly(ethylene oxide) (PEO), known to promote ionic conductivity, and the hard "A" block is a CO2-derived polycarbonate, poly(4-vinyl cyclohexene oxide carbonate), which provides mechanical rigidity and enhances oxidative stability. ABA block polymers featuring controllable PEO and polycarbonate lengths are straightforwardly prepared using hydroxyl telechelic PEO as a macroinitiator for CO2/epoxide ring-opening copolymerization and a well-controlled Mg(II)Co(II) catalyst. The influence of block polymer composition upon electrochemical and mechanical properties is investigated, with phosphonic acid functionalities being installed in the polycarbonate domains for adhesive properties. Three lead polymer materials are identified; these materials show an ambient ionic conductivity of 10 -4 S cm-1, lithium-ion transport (tLi+ 0.3-0.62), oxidative stability (>4 V vs Li+/Li), and elastomeric or plastomer properties (G' 0.1-67 MPa). The best block polymers are used in composite cathodes with LiNi0.8Mn0.1Co0.1O2 active material and Li6PS5Cl solid electrolyte-the resulting solid-state batteries demonstrate greater capacity retention than equivalent cells featuring no polymer or commercial polyelectrolytes.

Achieving Ultrahigh-Rate Planar and Dendrite-Free Zinc Electroplating for Aqueous Zinc Battery Anodes.

Despite being one of the most promising candidates for grid-level energy storage, practical aqueous zinc batteries are limited by dendrite formation, which leads to significantly compromised safety and cycling performance. In this study, by using single-crystal Zn-metal anodes, reversible electrodeposition of planar Zn with a high capacity of 8 mAh cm-2 can be achieved at an unprecedentedly high current density of 200 mA cm-2 . This dendrite-free electrode is well maintained even after prolonged cycling (>1200 cycles at 50 mA cm- 2 ). Such excellent electrochemical performance is due to single-crystal Zn suppressing the major sources of defect generation during electroplating and heavily favoring planar deposition morphologies. As so few defect sites form, including those that would normally be found along grain boundaries or to accommodate lattice mismatch, there is little opportunity for dendritic structures to nucleate, even under extreme plating rates. This scarcity of defects is in part due to perfect atomic-stitching between merging Zn islands, ensuring no defective shallow-angle grain boundaries are formed and thus removing a significant source of non-planar Zn nucleation. It is demonstrated that an ideal high-rate Zn anode should offer perfect lattice matching as this facilitates planar epitaxial Zn growth and minimizes the formation of any defective regions.

Temperature Dependence of Lithium Anode Voiding in Argyrodite Solid-State Batteries.

Void formation at the Li/ceramic electrolyte interface of an all-solid-state battery on discharge results in high local current densities, dendrites on charge, and cell failure. Here, we show that such voiding is reduced at the Li/Li6PS5Cl interface at elevated temperatures, sufficient to increase the critical current before voiding and cell failure from <0.25 mA cm-2 at 25 °C to 0.25 mA cm-2 at 60 °C and 0.5 mA cm-2 at 80 °C under a relatively low stack-pressure of 1 MPa. Increasing the stack-pressure to 5 MPa and temperature to 80 °C permits stable cycling at 2.5 mA cm-2. It is also shown that the charge-transfer resistance at the Li/Li6PS5Cl interface depends on pressure and temperature, with relatively high pressures required to maintain low charge-transfer resistance at -20 °C. These results are consistent with the plastic deformation of Li metal dominating the performance of the Li anode, posing challenges for the implementation of solid-state cells with Li anodes.

Covalency does not suppress O2 formation in 4d and 5d Li-rich O-redox cathodes.

Layered Li-rich transition metal oxides undergo O-redox, involving the oxidation of the O2- ions charge compensated by extraction of Li+ ions. Recent results have shown that for 3d transition metal oxides the oxidized O2- forms molecular O2 trapped in the bulk particles. Other forms of oxidised O2- such as O22- or (O-O)n- with long bonds have been proposed, based especially on work on 4 and 5d transition metal oxides, where TM-O bonding is more covalent. Here, we show, using high resolution RIXS that molecular O2 is formed in the bulk particles on O2‒ oxidation in the archetypal Li-rich ruthenates and iridate compounds, Li2RuO3, Li2Ru0.5Sn0.5O3 and Li2Ir0.5Sn0.5O3. The results indicate that O-redox occurs across 3, 4, and 5d transition metal oxides, forming O2, i.e. the greater covalency of the 4d and 5d compounds still favours O2. RIXS and XAS data for Li2IrO3 are consistent with a charge compensation mechanism associated primarily with Ir redox up to and beyond the 5+ oxidation state, with no evidence of O-O dimerization.

Visualizing plating-induced cracking in lithium-anode solid-electrolyte cells.

Lithium dendrite (filament) propagation through ceramic electrolytes, leading to short circuits at high rates of charge, is one of the greatest barriers to realizing high-energy-density all-solid-state lithium-anode batteries. Utilizing in situ X-ray computed tomography coupled with spatially mapped X-ray diffraction, the propagation of cracks and the propagation of lithium dendrites through the solid electrolyte have been tracked in a Li/Li6PS5Cl/Li cell as a function of the charge passed. On plating, cracking initiates with spallation, conical 'pothole'-like cracks that form in the ceramic electrolyte near the surface with the plated electrode. The spallations form predominantly at the lithium electrode edges where local fields are high. Transverse cracks then propagate from the spallations across the electrolyte from the plated to the stripped electrode. Lithium ingress drives the propagation of the spallation and transverse cracks by widening the crack from the rear; that is, the crack front propagates ahead of the Li. As a result, cracks traverse the entire electrolyte before the Li arrives at the other electrode, and therefore before a short circuit occurs.

Non-equilibrium metal oxides via reconversion chemistry in lithium-ion batteries.

Binary metal oxides are attractive anode materials for lithium-ion batteries. Despite sustained effort into nanomaterials synthesis and understanding the initial discharge mechanism, the fundamental chemistry underpinning the charge and subsequent cycles-thus the reversible capacity-remains poorly understood. Here, we use in operando X-ray pair distribution function analysis combining with our recently developed analytical approach employing Metropolis Monte Carlo simulations and non-negative matrix factorisation to study the charge reaction thermodynamics of a series of Fe- and Mn-oxides. As opposed to the commonly believed conversion chemistry forming rocksalt FeO and MnO, we reveal the two oxide series topotactically transform into non-native body-centred cubic FeO and zincblende MnO via displacement-like reactions whose kinetics are governed by the mobility differences between displaced species. These renewed mechanistic insights suggest avenues for the future design of metal oxide materials as well as new material synthesis routes using electrochemically-assisted methods.