Dense, Regular GaAs Nanowire Arrays by Catalyst-Free Vapor Phase Epitaxy for Light Harvesting.

Density dependent growth and optical properties of periodic arrays of GaAs nanowires (NWs) by fast selective area growth MOVPE are investigated. As the period of the arrays is decreased from 500 nm down to 100 nm, a volume growth enhancement by a factor of up to four compared with the growth of a planar layer is observed. This increase is explained as resulting from increased collection of precursors on the side walls of the nanowires due to the gas flow redistribution in the space between the NWs. Normal spectral reflectance of the arrays is strongly reduced compared with a flat substrate surface in all fabricated arrays. Electromagnetic modeling reveals that this reduction is caused by antireflective action of the nanowire arrays and nanowire-diameter dependent light absorption. Irrespective of the periodicity and diameter, Raman scattering and grazing angle X-ray diffraction show signal from zinc blende and wurtzite phases, the latter originating from stacking faults as observed by high resolution transmission electron microscopy. Raman spectra contain intense surface phonons peaks, whose intensity depends strongly on the nanowire diameters as a result of potential structural changes and as well as variations of optical field distribution in the nanowires.

Antibacterial activity of microstructured Ag/Au sacrificial anode thin films.

Ten different Ag dot arrays (16 to 625 microstructured dots per square mm) were fabricated on a continuous Au thin film and for comparison also on Ti film by sputter deposition and photolithographic patterning. To analyze the antibacterial activity of these microstructured films Escherichia coli and Staphylococcus aureus were placed onto the array surfaces and cultivated overnight. To analyze the viability of planktonic as well as surface adherent bacteria, the applied bacterial fluid was subsequently aspirated, plated on blood agar plates and adherent bacteria were detected by fluorescence microscopy. A particular antibacterial effect towards both bacterial strains was induced by Ag dot arrays on fabricated Au thin film (sacrificial anode system for Ag), due to the release of Ag ions from dissolution of Ag dots in contrast to Ag dot arrays fabricated on the Ti thin films (non-sacrificial anode system for Ag) which remained intact to the original dot shape. The required number of Ag dots on gold film to achieve complete bactericidal effects for both bacterial strains was seven times lower than that observed with Ag dot arrays on Ti film.