Tuning Coherent-Phonon Heat Transport in LaCoO3/SrTiO3 Superlattices.

Accessing the regime of coherent phonon propagation in nanostructures opens enormous possibilities to control the thermal conductivity in energy harvesting devices, phononic circuits, etc. In this paper we show that coherent phonons contribute substantially to the thermal conductivity of LaCoO3/SrTiO3 oxide superlattices, up to room temperature. We show that their contribution can be tuned through small variations of the superlattice periodicity, without changing the total superlattice thickness. Using this strategy, we tuned the thermal conductivity by 20% at room temperature. We also discuss the role of interface mixing and epitaxial relaxation as an extrinsic, material dependent key parameter for understanding the thermal conductivity of oxide superlattices.

Sub-µL measurements of the thermal conductivity and heat capacity of liquids.

We present the analysis of the thermal conductivity, κ, and heat capacity, Cp, of a wide variety of liquids, covering organic molecular solvents, ionic liquids and water-polymer mixtures. These data were obtained from ≈0.6 µL samples, using an experimental development based on the 3ω method, capable of the simultaneous measurement of κ and Cp. In spite of the different type and strength of interactions, expected in a priori so different systems, the ratio of κ to the sound velocity is approximately constant for all of them. This is the consequence of a similar atomic density for all these liquids, notwithstanding their different molecular structures. This was corroborated experimentally by the observation of a Cp/V ≈ 1.89 × 106 J K-1 m-3 (≈3R/2 per atom), for all liquids studied in this work. Finally, the very small volume of the sample required in this experimental method is an important advantage for the characterization of systems like nanofluids, in which having a large amount of the dispersed phase is sometimes extremely challenging.