Redox Exfoliation of Layered Transition Metal Dichalcogenides.

Transition metal dichalcogenides (TMDs) have attracted considerable attention in a diverse array of applications due to the breadth of possible property suites relative to other low-dimensional nanomaterials (e.g., graphene, aluminosilicates). Here, we demonstrate an alternative methodology for the exfoliation of bulk crystallites of group V-VII layered TMDs under quiescent, benchtop conditions using mild redox chemistry. Anionic polyoxometalate species generated from edge sites adsorb to the TMD surface and create Coulombic repulsion that drives layer separation without the use of shear forces. This method is generalizable (MS2, MSe2, and MTe2) and effective in preparing high-concentration (>1 mg/mL) dispersions with narrow layer thickness distributions more rapidly and with safer reagents than alternative solution-based approaches. Finally, exfoliation of these TMDs is demonstrated in a range of solvent systems that were previously inaccessible due to large surface energy differences. These characteristics could be beneficial in the preparation of high-quality films and monoliths.

Thermal anisotropy in nano-crystalline MoS2 thin films.

In this work, we grow thin MoS2 films (50-150 nm) uniformly over large areas (>1 cm(2)) with strong basal plane (002) or edge plane (100) orientations to characterize thermal anisotropy. Measurement results are correlated with molecular dynamics simulations of thermal transport for perfect and defective MoS2 crystals. The correlation between predicted (simulations) and measured (experimental) thermal conductivity are attributed to factors such as crystalline domain orientation and size, thereby demonstrating the importance of thermal boundary scattering in limiting thermal conductivity in nano-crystalline MoS2 thin films. Furthermore, we demonstrate that the cross-plane thermal conductivity of the films is strongly impacted by exposure to ambient humidity.

Pulsed laser syntheses of layer-structured WS2 nanomaterials in water.

We used water as an environmental friendly medium for the synthesis of hexagonal WS2 nanoparticles by the pulsed laser method. The materials collected on substrates were oriented with the 2H-WS2 basal planes parallel to the surface. The use of water, UV lasers, and large WS2 targets prevented the nanoparticles from restructuring into inorganic fullerenes, which were observed in research using hydrocarbon solvents, longer wavelength lasers, and dispersed powder targets. Fairly good dispersion of nanoparticles suggests that large surface areas are available for chemical reactivity.