ABSTRACT
In this work, we describe an experimental setup for a spatially resolved pump-probe experiment with an integrated wide-field magneto-optical (MO) microscope. The MO microscope can be used to study ferromagnetic materials with both perpendicular-to-plane and in-plane magnetic anisotropy via polar Kerr and Voigt effects, respectively. The functionality of the Voigt effect-based microscope was tested using an in-plane magnetized ferromagnetic semiconductor (Ga,Mn)As. It was revealed that the presence of mechanical defects in the (Ga,Mn)As epilayer alters significantly the magnetic anisotropy in their proximity. The importance of MO experiments with simultaneous temporal and spatial resolutions was demonstrated using a (Ga,Mn)As sample attached to a piezoelectric transducer, which produces a voltage-controlled strain. We observed a considerably different behavior in different parts of the sample that enabled us to identify sample parts where the epilayer magnetic anisotropy was significantly modified by the presence of the piezoelectric transducer and where it was not. Finally, we discuss the possible applicability of our experimental setup for the research of compensated antiferromagnets, where only MO effects even in magnetic moments are present.
ABSTRACT
We report on a systematic study of the stress transferred from an electromechanical piezo-stack into GaAs wafers under a wide variety of experimental conditions. We show that the strains in the semiconductor lattice, which were monitored in situ by means of X-ray diffraction, are strongly dependent on both the wafer thickness and on the selection of the glue which is used to bond the wafer to the piezoelectric actuator. We have identified an optimal set of parameters that reproducibly transfers the largest distortions at room temperature. We have studied strains produced not only by the frequently used uniaxial piezostressors but also by the biaxial ones which replicate the routinely performed experiments using substrate-induced strains but with the advantage of a continuously tunable lattice distortion. The time evolution of the strain response and the sample tilting and/or bending are also analyzed and discussed.
ABSTRACT
(Ga,Mn)As is at the forefront of spintronics research exploring the synergy of ferromagnetism with the physics and the technology of semiconductors. However, the electronic structure of this model spintronics material has been debated and the systematic and reproducible control of the basic micromagnetic parameters and semiconducting doping trends has not been established. Here we show that seemingly small departures from the individually optimized synthesis protocols yield non-systematic doping trends, extrinsic charge and moment compensation, and inhomogeneities that conceal intrinsic properties of (Ga,Mn)As. On the other hand, we demonstrate reproducible, well controlled and microscopically understood semiconducting doping trends and micromagnetic parameters in our series of carefully optimized epilayers. Hand-in-hand with the optimization of the material synthesis, we have developed experimental capabilities based on the magneto-optical pump-and-probe method that allowed us to simultaneously determine the magnetic anisotropy, Gilbert damping and spin stiffness constants from one consistent set of measured data.