ABSTRACT
The complete ZnS xSe1- x solid solution was successfully obtained by the mechanochemical process denoted as a mechanically induced self-sustaining reaction. Excellent control of the chemical stoichiometry of the solid solution was possible by adjusting the atomic ratio of the starting Zn/S/Se elemental mixture subjected to milling. A mixture of both wurtzite-2H (hexagonal) and zinc blende (cubic) structures was always obtained, although for a similar milling time the proportion of the zinc blende structure increased with the Se content in the solid solution. However, wurtzite was the major phase for S-rich compositions when milling was stopped just after ignition. It was demonstrated that milling induces the wurtzite-to-zinc blende phase transition. The 8H hexagonal polytype was also observed in samples subjected to long milling times. Variation of the lattice parameters for both structures with the x value in the solid solution presented an excellent linearity, confirming the validity of Vegard's law. However, variation of the band-gap energy ( Eg) with x was not perfectly linear, and a small bowing parameter of 0.34 was obtained. It was possible to tune the Eg value between those of the end members of the solid solution in a continuous manner by adjusting the stoichiometry of the solid solution. The morphology and crystalline domain size can also be controlled by adjusting, in this case, the postignition milling time of the mechanochemical process.
ABSTRACT
In this work, a gas flow sputtering (GFS) process which allows the production and deposition of metal nanoparticles (NPs) in a vacuum environment is described. Aim of the study is to prove the potential of this technology for the fabrication of new TiO2 films with enhanced photocatalytic properties. For this purpose, Ag and Pt NPs have been produced and deposited on photocatalytic float glass coated with TiO2 thin films by magnetron sputtering. The influence of the process parameters and of the metal amount on the final properties of the particles (quantity, size, size distribution, oxidation state etc.,) was widely investigated. Moreover, the effect of the NPs on the photocatalytic activity of the resulting materials was evaluated for the case of the decomposition of stearic acid (SA) during UV-A irradiation. The reduction of the water contact angle (WCA) during the irradiation period was measured in order to test the photo-induced super-hydrophilicity (PSH).
ABSTRACT
Dispersed SBA-15 rods have been synthesized with varying lengths, widths, and pore sizes in a low-temperature synthesis in the presence of heptane and NH(4)F. The pore size of the material can systematically be varied between 11 and 17 nm using different hydrothermal treatment times and/or temperatures. The particle length (400-600 nm) and width (100-400 nm) were tuned by varying the HCl concentration. All the synthesized materials possess a large surface area of 400-600 m(2)/g and a pore volume of 1.05-1.30 cm(3). A mechanism for the effect of the HCl concentration on the particle morphology is suggested. Furthermore, it is shown that the reaction time can be decreased to 1 h, with well-retained pore size and morphology. This work has resulted in SBA-15 rods with the largest pore size reported for this morphology.