ABSTRACT
Developing facile methods for the synthesis of active and stable electrocatalysts is vitally important to realize overall water splitting. Here, we demonstrate a practical method to obtain FeNiOOH nanosheets on nickel foam (NF) as bifunctional electrocatalyst by growing a FeCo Prussian blue analog with further in situ oxidation under ambient conditions. The binder-free, self-standing FeNiOOH/NF electrode with hierarchical nanostructures requires low overpotentials of 260 mV and 240 mV at a current density of 50 mA cm-2 for oxygen evolution reaction and hydrogen evolution reaction, respectively, in 1.0 M KOH solution. Therefore, an alkaline water electrolyzer constructed by bifunctional FeNiOOH/NF electrode as both anode and cathode delivers 50 mA cm-2 under a cell voltage of 1.74 V with remarkable stability, which outperforms the IrO2-Pt/C-based electrolyzer. The excellent performance could be ascribed to the superior FeNiOOH intrinsic activity and the hierarchical structure. This work provides a cost-efficient surface engineering method to obtain binder-free, self-standing bifunctional electrocatalyst on commercial NF, which could be further extended to other energy and environment applications.
ABSTRACT
Incorporation of ultrathin nanosheets with dopants/defects shows great potential to enable metal (oxy)-hydroxide electrocatalysts with enhanced oxygen evolution reaction (OER) performance via the regulation of atomic structure and bonding arrangements. However, it remains challenging in synthesis especially for such dual control and at large scale. In this study, we present a stepwise chemical oxidation route, involving phase transition and reconstruction processes, to access ultrathin CoOOH nanosheets with a thickness of ca. 4 nm and abundant oxygen vacancies. Other transition metals were also doped into CoOOH nanosheets through this strategy. Among them, the optimized FeCoOOH nanosheets demonstrated an efficient OER activity with overpotential as low as 252 mV (current density: 10 mA cm-2) and excellent stability. A high and stable solar-to-hydrogen efficiency of 10.5% was acquired when FeCoOOH nanosheets were used as the anode in a constructed water splitting device driven by solar energy. This study offers a noble and facile strategy for potentially scalable preparation of atom-modulated ultrathin metal (oxy)-hydroxide nanosheets, and also demonstrates the OER applications.