Optimization and Evaluation of Accelerated Corrosion Tests Based on Mechanism Equivalence Principles.

Conventional indoor corrosion test design methods primarily focus on the rapid evaluation of material corrosion resistance, often neglecting the impact of environmental stress levels on the equivalence of corrosion mechanisms. This study introduces a novel indoor corrosion test design method based on the principle of corrosion mechanism equivalence, aimed at improving the accuracy of indoor accelerated corrosion simulations. We define the characteristic of corrosion mechanism equivalence as the Corrosion Mechanism Equivalence Degree (CMed), which quantifies the similarity between corrosion mechanisms in indoor accelerated tests and field tests. Then, modified conventional link function models are defined, integrating the probability distribution of environmental factors to estimate corrosion model parameters more precisely. Finally, an optimization problem is constructed for accelerated corrosion tests based on CMed, incorporating constraints on environmental stress levels and acceleration factors. A case study demonstrates the proposed method's ability to accurately simulate the actual service environment of materials, determining the appropriate stress levels for indoor accelerated corrosion tests while ensuring the desired acceleration factor and corrosion mechanism equivalence.

Corrosion Behavior and Mechanical Properties of 30CrMnSiA High-Strength Steel under an Indoor Accelerated Harsh Marine Atmospheric Environment.

In this work, the corrosion behavior and mechanical properties of 30CrMnSiA high-strength steel under a harsh marine atmosphere environment were systematically studied using accelerated test technology, along with corrosion kinetic analysis, microstructure and phase composition analysis, electrochemical measurements, and mechanical property tests. The influence of corrosion time on corrosion kinetics was characterized by the weight loss method. The corrosion layer and its product evolution were analyzed by SEM, EDS, XRD, and XPS. The corrosion behavior of steel was studied by a potentiodynamic polarization curve and EIS. Finally, the influence of corrosion on mechanical properties was studied by tensile and fatigue tests. The results show that 30CrMnSiA high strength steel has good corrosion resistance in a harsh marine atmosphere environment. Its corrosion behavior is cyclical: the outer rust layer exfoliated, the inner rust layer became the outer rust layer, and the matrix became inner rust due to the attack by the corrosive medium. The rust layer had a great protective effect on the matrix. The mechanical properties of 30CrMnSiA high-strength steel were reduced under the corrosive environment, and corrosion had a significant effect on its fatigue resistance.