ABSTRACT
INTRODUCTION: Peripheral nerve disruptions, frequently occurring during limb injuries, give rise to serious complications of patients recovery resulting from limitations in neural tissue regeneration capabilities. To overcome this problem bridging techniques utilizing guidance channels gain their importance. Biodegradable polymeric tubes seem to be more prospective then non-degradable materials - no necessity of implant removal and possibilities of release of incorporated drugs or biologically active agents that may support nerve regeneration process are the main advantages. MATERIAL AND METHODS: Polymer blend of commercial poly(L-lactic acid) (PLLA) and in-house synthesized poly(trimethylene carbonate) (PTMC) were processed in an organic solvent - phase inversion process on a supporting rod - to form a guidance porous tube of 1.1 mm inner diameter. In vivo experiments on rat's cut femoral nerve by using either the tubes or end-to-end suturing (control group) involved 22 and 19 rats, respectively. Motor recovery of operated limbs, neuroma occurrence and histopathology of explanted nerves were evaluated after 30, 60 and 90 days of implantation. RESULTS: Motor recovery of the limbs was of similar rate for the two animal groups. The neuroma formation was evident in over 90% control specimens, while for the bridging group it was less than 40% of all evaluable samples (p = 0.0022). Biocompatibility of applied materials was affirmed by moderate tissue response. CONCLUSIONS: Application of the biodegradable PLLA/PTMC polymeric tubes effectively supports regeneration of discontinued nerves. The applied material prevents neuroma formation, by reducing the scar tissue formation time and, thus, accelerating the process of neural tissue restoration.
ABSTRACT
INTRODUCTION: The subject of the experiment was bacterial nanocellulose, a natural polymer produced by bacteria - Gluconacetobacter xylinus. Following a specific modification process a cartilage-like material for restoration of damaged tissues may be produced. The obtained implants with excellent biocompatibility, mouldability, biophysical and chemical properties perfectly fit the needs of reconstructive surgery. The goal of the experiment was to develop and analyze cellulosic guidance channels in vivo for the reconstruction of damaged peripheral nerves. MATERIAL AND METHODS: The experiments were conducted on Wistar rats, femoral nerve. Cellulose was produced according to a self-patented method. In the experimental group tubulization was applied, whereas in the control traditional end-to-end connection was used. Observation time was 30, 60, 90, and 180 days. Results evaluation included histological analysis and postoperative observation of motor recovery. RESULTS: The overgrowth of connective tissue and disorganisation of neural structures was evident in 86.67% of control specimens, while for cellulosic group it was only 35% (p = 0.0022). Tubulization prevented the excessive proliferation of connective tissue and isolated from penetration with scar tissue. Autocannibalism, being probably an evidence of neurotrophic factors amassment, was observed in cellulosic group but not in the control one. Motor recovery did not differ significantly (p > 0.05). Biocompatibility of implants was affirmed by very small level of tissue response and susceptibility to vascularisation. CONCLUSIONS: Cellulosic neurotubes effectively prevent the formation of neuromas. They are of very good biocompatibility and allow the accumulation of neurotrophic factors inside, thus facilitating the process of nerve regeneration.
