Epitaxial graphene homogeneity and quantum Hall effect in millimeter-scale devices.

Quantized magnetotransport is observed in 5.6 × 5.6 mm2 epitaxial graphene devices, grown using highly constrained sublimation on the Si-face of SiC(0001) at high temperature (1900 °C). The precise quantized Hall resistance of [Formula: see text] is maintained up to record level of critical current Ixx = 0.72 mA at T = 3.1 K and 9 T in a device where Raman microscopy reveals low and homogeneous strain. Adsorption-induced molecular doping in a second device reduced the carrier concentration close to the Dirac point (n ≈ 1010 cm-2), where mobility of 18760 cm2/V is measured over an area of 10 mm2. Atomic force, confocal optical, and Raman microscopies are used to characterize the large-scale devices, and reveal improved SiC terrace topography and the structure of the graphene layer. Our results show that the structural uniformity of epitaxial graphene produced by face-to-graphite processing contributes to millimeter-scale transport homogeneity, and will prove useful for scientific and commercial applications.

Fe-catalyzed etching of exfoliated graphite through carbon hydrogenation.

We present an investigation on Fe-catalyzed etching of graphite by dewetting Fe thin films on graphite in forming gas. Raman mapping of the etched graphite shows thickness variation in the etched channels and reveals that the edges are predominately terminated in zigzag configuration. X-ray diffraction and photoelectron spectroscopy measurements identify that the catalytic particles are Fe with the presence of iron carbide and iron oxides. The existence of iron carbide indicates that, in additional to carbon hydrogenation, carbon dissolution into Fe is also involved during etching. Furthermore, the catalytic particles can be re-activated upon a second annealing in forming gas.

Toward clean and crackless transfer of graphene.

We present the results of a thorough study of wet chemical methods for transferring chemical vapor deposition grown graphene from the metal growth substrate to a device-compatible substrate. On the basis of these results, we have developed a "modified RCA clean" transfer method that has much better control of both contamination and crack formation and does not degrade the quality of the transferred graphene. Using this transfer method, high device yields, up to 97%, with a narrow device performance metrics distribution were achieved. This demonstration addresses an important step toward large-scale graphene-based electronic device applications.

Superior thermal conductivity of single-layer graphene.

We report the measurement of the thermal conductivity of a suspended single-layer graphene. The room temperature values of the thermal conductivity in the range approximately (4.84+/-0.44)x10(3) to (5.30+/-0.48)x10(3) W/mK were extracted for a single-layer graphene from the dependence of the Raman G peak frequency on the excitation laser power and independently measured G peak temperature coefficient. The extremely high value of the thermal conductivity suggests that graphene can outperform carbon nanotubes in heat conduction. The superb thermal conduction property of graphene is beneficial for the proposed electronic applications and establishes graphene as an excellent material for thermal management.