Aquivion-Based Spray Freeze-Dried Composite Materials for the Cascade Production of γ-Valerolactone.

The development of multifunctional catalysts is a necessary step to effectively carry out one-pot cascade reactions, such as that from furfural to γ-valerolactone. This research effort faces the challenge posed by the intrinsic limit of how many kinds of catalytic sites a single material can bear. In this work, the application of Spray-Freeze Drying (SFD) as a synthetic technique for the preparation of a wide range of innovative composite multi-functional catalysts is reported. Herein we show that by the proper combination of Aquivion as a highly active Brønsted acid catalyst and metal oxides as both support materials and Lewis acids (LAS) enable to achieve highly unique efficient and effective dual acid composite catalysts that are able to carry out the cascade reaction from furfural to γ-valerolactone. The dual catalytic system comprised of Aq/ZrO2 with 30 % polymer content prepared via spray-freeze drying exhibited GVL yields of 25 % after only 2 h at 180 °C and a remarkably high productivity of 4470 µmolGVL gCat -1 h-1, one of the highest reported results. Mechanistic studies based on experimental and advanced characterisation and spectroscopic techniques, such as, SEM, TEM, 15N MAS NMR and 19F MAS NMR indicate that activity arises from the proper tuning of BAS/LAS (Brønsted Acid Site/Lewis Acid Site) acidic properties.

Solid-state NMR characterization of the structure and thermal stability of hybrid organic-inorganic compounds based on a HLaNb2O7 Dion-Jacobson layered perovskite.

Dion-Jacobson phases, like MLaNb2O7, are an interesting class of ion-exchangeable layered perovskites possessing electronic and photocatalytic properties. Their protonated and organo-modified homologues, in particular, have already been indicated as promising catalysts. However, the structural analysis of these highly tailorable materials is still incomplete, and both the intercalation process and thermal stability of the included organic moieties are far from being completely understood. In this study, we present a thorough solid-state NMR characterization of HLaNb2O7·xH2O intercalated with different amounts of octylamine, or with decylamine. Samples were analyzed as prepared, and after thermal treatment at different temperatures up to 220 °C. The substitution of pristine proton ions was followed via(1)H MAS NMR spectroscopy, whereas the alkyl chains were monitored through (13)C((1)H) CP MAS experiments. The interactions in the interlayer space were explored using (13)C((1)H) 2D heteronuclear correlation experiments. We demonstrate that some of the protons are involved in the functionalization reaction, and some of them are in close proximity to the alkyl ammonium chains. Heating of the hybrid materials leads first to a rearrangement of the alkyl chains and then to their degradation. The spatial arrangement of the chains, their interactions and the thermal behavior of the materials depend on the extent of the functionalization, and on the nature of the intercalated alkyl ammonium ions.