Physical Properties and the Reconstruction of Unstable Decahedral Silver Nanoparticles Synthesized Using Plasmon-Mediated Photochemical Process.

Plasmon-mediated shape transformation from quasi-spherical silver nanoparticles (AgNPs) to silver nanoprisms (AgNPrs) and decahedral silver nanoparticles (D-AgNPs) under irradiation of blue LEDs (λ = 456 ± 12 nm, 80 mW/cm2) was studied at temperatures ranging between 60, 40, 30, 20, 10, and 0 °C. It was found that reaction temperature affected transformation rates and influenced the morphology distribution of final products. The major products synthesized at temperatures between 60 °C and 0 °C were AgNPrs and D-AgNPs, respectively. The D-AgNPs synthesized at such low temperatures are unstable and become blunt when light irradiation is removed after the photochemical synthesis. These blunt nanoparticles with pentagonal multiple-twinned structures can be further used as the seeds to reconstruct complete D-AgNPs after irradiating blue LEDs at various bath temperatures. Our results showed that these rebuilt D-AgNPs are much more stable when at higher bath temperatures. Furthermore, the rebuilt D-AgNPs (edge lengths ~41 nm) can grow into larger D-AgNPs (edge lengths ~53 nm) after the irradiation of green LEDs. Surface-enhanced Raman spectra of CV in AgNP colloids showed that D-AgNP colloids have better SERS enhancements factors than AgNPrs.

Influence of Temperature on the Formation of Silver Nanoparticles by using a Seed-Free Photochemical Method under Sodium-Lamp Irradiation.

Silver nanoparticles can be prepared by using a seed-free photo-assisted citrate reduction method under the irradiation of a sodium lamp. Under the same irradiation intensity, bath temperatures are crucial in influencing the reaction rate, morphologies of final products, and shape evolution of the silver nanostructures. For example, when the bath temperature is 80 °C, the product yields of silver nanoplates, nanorods, and nanodecahedra are 38±6 %, 35±10 %, and 12±8 %, respectively. However, when the bath temperature is 30 °C, the product yields of silver nanoplates, nanorods, and nanodecahedra are 6±3 %, 0 %, and 83±16 %, respectively. Time-dependent UV/Vis spectra and TEM images show that silver nanoplates were formed at the earlier reaction stage and greatly decreased in amount at the later stage when the bath temperatures are less than or equal to 40 °C. This indicates that the silver nanoplates, which can be regarded as intermediates, are kinetically favored products. They are not thermodynamically favored products at these relatively low bath temperatures. The SERS spectra of crystal violet (CV) show that all the silver colloids synthesized at various temperatures exhibit good enhancement factors and that the colloids prepared at lower bath temperatures have a higher enhancement factor.

Effect of Temperature on the Growth of Silver Nanoparticles Using Plasmon-Mediated Method under the Irradiation of Green LEDs.

Plasmon-mediated shape conversion of spherical silver nanoparticles (NPs) to nanostructures with other shapes under the irradiation of green LEDs (520 ± 20 nm, 35 mw/cm²) at various temperatures (60, 40, 20, 10, 5, and 0 °C) was performed in this study. It was found that the bath temperature used in the reaction can influence the reaction rates, i.e., the times needed for the shape transformation process were 5, 11.5, 25, 45, 72, and 100 h at 60, 40, 20, 10, 5, and 0 °C, respectively. In addition, the bath temperature can also alter the morphologies of the final products. The major products are silver nanoplates at 60, 40 and 20 °C. However, they became decahedral silver NPs at 5 and 0 °C. The percentages of decahedral silver NPs synthesized at 60, 40, 20, 10, 5, and 0 °C are 0%, 1%, 5%, 45%, 73%, and 89%, respectively. Measuring the surface-enhanced Raman spectroscopy (SERS) spectra of the probe molecule R6G in the presence of KBr showed that both silver nanoplate colloids synthesized at 60 °C and decahedral silver NP colloids synthesized at 0 °C in the absence of PVP had good SERS activities.