ABSTRACT
We investigated the heat dissipation in heterostructure field-effect transistors (HFETs) using microRaman measurement of the temperature in active AIGaN/GaN. By varying the gate structure, the heat dissipation through the gate was clearly revealed. The temperature increased to 120 °C at the flat gate device although the inserted gate increased to only 37 °C. Our results showed that the inserted gate structure reduced the self-heating effect by three times compared to the flat gate structure. Temperature mapping using micro-Raman measurement confirmed that the temperature of the near gate area was lower than that of the near drain area. This indicated that the inserted gate electrode structure effectively prohibited self-heating effects.
ABSTRACT
Various postsynthesis processes for transition metal dichalcogenides have been attempted to control the layer number and defect concentration, on which electrical and optical properties strongly depend. In this work, we monitored changes in the photoluminescence (PL) of molybdenum disulfide (MoS2) until laser irradiation generated defects on the sample flake and completely etched it away. Higher laser power was required to etch bilayer MoS2 compared to monolayer MoS2. When the laser power was 270 µW with a full width at half-maximum of 1.8 µm on bilayer MoS2, the change in PL intensity over time showed a double maximum during laser irradiation due to a layer-by-layer etching of the flake. When the laser power was increased to 405 µW, however, both layers of bilayer MoS2 were etched all at once, which resulted in a single maximum in the change of PL intensity over time, as in the case of monolayer MoS2. The dependence of the etching pattern for bilayer MoS2 on laser power was also reflected in position changes of both exciton and trion PL peaks. The subtle changes in the PL spectra of MoS2 as a result of laser irradiation found here are discussed in terms of PL quantum efficiency, conversion between trions and excitons, mean interatomic spacing, and the screening of Coulomb interaction.
ABSTRACT
We investigated the homogeneity and tolerance to heat of monolayer MoS2 using photoluminescence (PL) spectroscopy. For MoS2 on SiO2, the PL spectra of the basal plane differ from those of the edge, but MoS2 on hexagonal boron nitride (h-BN) was electron-depleted with a homogeneous PL spectra over the entire area. Annealing at 450 °C rendered MoS2 on SiO2 homogeneously electron-depleted over the entire area by creating numerous defects; moreover, annealing at 550 °C and subsequent laser irradiation on the MoS2 monolayer caused a loss of its inherent crystal structure. On the other hand, monolayer MoS2 on h-BN was preserved up to 550 °C with its PL spectra not much changed compared with MoS2 on SiO2. We performed an experiment to qualitatively compare the binding energies between various layers, and discuss the tolerance of monolayer MoS2 to heat on the basis of interlayer/interfacial binding energy.
ABSTRACT
van der Waals (vdW) heterostructures with two-dimensional (2D) crystals such as graphene, hexagonal boron nitride (hBN) and transition metal dichalcogenides (TMDCs) allow us to demonstrate atomically thin field-effect transistors (FETs), photodetectors (PDs) and photovoltaic devices capable of higher performance and greater stability levels than conventional devices. Although there have been studies of gas molecule sensing with 2D crystal channels, vdW heterostructures based on 2D crystals have not been employed thus far. Here, utilizing graphene/WS2/graphene (G/WS2/G) vdW heterostructure tunnel FETs, we demonstrate the rectification behavior of the sensitivity signal by tuning the WS2 potential barriers as a function of the gas molecule concentration and devise a fingerprint map of the sensitivity variation corresponding to an individual ratio of two different molecules in a gas mixture. Because the separation of different gas molecule concentrations from gas mixtures is in high demand in the gas-sensing research field, this result will greatly assist in the progress on selective gas sensing.
ABSTRACT
The position of a single GaAs quantum dot (QD), which is optically active, grown by low-density droplet epitaxy (DE) (approximately 4 QDs/µm(2)), was directly observed on the surface of a 45-nm-thick Al0.3Ga0.7As capping layer. The thin thickness of AlGaAs capping layer is useful for single photon sources with plasmonic optical coupling. A micro-photoluminescence for GaAs DE QDs has shown exciton/biexciton behavior in the range of 1.654 to 1.657 eV. The direct observation of positions of low-density GaAs DE QDs would be advantageous for mass fabrication of devices that use a single QD, such as single photon sources.