ABSTRACT
In the optical energy gap, visible and near-IR emission of halide phosphate glasses with a composition of 40P2O5-30ZnO-20LiCl-10BaF2 in mol% doped with 3.5 × 104 ppm Pr2O3, referred to as PZLBPr, were synthesized. The UV-VIS-NIR and spectroscopic properties of these glasses were also predicted. The current glasses had broadband emission photoluminescence covering a wavelength range of 1250 to 1700 nm when excited at 455 nm. These bands for near-infrared emission luminescence relate to the transitions 1G4 â 3H5, 1D2 â 1G4, and 3H4 â 3F3, 3F4 in the optical telecommunication window. The significant PL emission wideband was caused by the radiative transition from Pr3+: 1D2 to 1G4. At 445 nm excitation, these glasses exhibited emission bands that corresponded to blue/reddish orange spectral ranges in visible ranges. The prepared glass has a high lasing quality factor (Ω4/Ω6 = 0.9), high optical energy (4.72 eV), and quantum efficiency = 87.3% with FWHM = 156 nm of transition emission from the 1D2 â 1G4 level. As a result, broadband near infrared optical amplifiers can be fabricated from the prepared glasses.