Facile synthesis of CaFe2O4 for visible light driven treatment of polluting palm oil mill effluent: Photokinetic and scavenging study.

In this paper, a facile synthesis method for CaFe2O4 is introduced that produces a catalyst capable of significant photocatalytic degradation of POME under visible light irradiation. The co-precipitation method was used to produce two catalysts at calcination temperatures of 550 °C and 700 °C dubbed CP550 and CP700. CP550 demonstrated the maximum COD removal of 69.0% at 0.75 g/L catalyst loading after 8 h of visible light irradiation which dropped to 61.0% after three consecutive cycles. SEM images indicated that the higher calcination temperature of CP700 led to annealing which reduced the pore volume (0.025 cm3/g) and pore diameter (10.3 nm) while simultaneously creating a smoother and more spherical surface with lower SBET (9.73 m2/g). In comparison, CP550 had a rough hair-like surface with higher SBET (27.28 m2/g) and pore volume (0.077 cm3/g) as evidenced by BET analysis. XRD data indicated the presence of CaFe5O7 in the CP550 composition which was not present in CP700. The presence of Wustite-like FeO structures in CaFe5O7 are likely the cause for lower photoluminescence intensity profile and hence better charge separation of CP550 as these structures in CaFe2O4 have been known to increase resistivity and electron localization. The COD removal of CP550 dropped from 69.0% to just 7.0% upon adding a small quantity of isopropanol into the reaction mixture indicating hydroxyl radicals as the primary reactive oxidative species.

Photocatalytic treatment of palm oil mill effluent by visible light-active calcium ferrite: Effects of catalyst preparation technique.

Palm oil mill effluent (POME) is a serious and expensive environmental problem in Malaysia. In this paper, CaFe2O4 is introduced as a novel photocatalyst for the degradation of POME under visible light irradiation. Two synthesis routes, auto-combustion and co-precipitation, and two calcination temperatures 550 °C and 700 °C were used to produce four CaFe2O4 catalysts AC550, AC700, CP550 and CP700. CP550 exhibited the greatest photocatalytic degradation at 56% chemical-oxygen-demand (COD) removal after 8 h of irradiation which dropped to 49% after three consecutive cycles indicating reasonable conversion and high recyclability. BET analysis indicated CP550 had the highest SBET (27.28 m2/g) and pore volume (0.077 cm3/g) which dropped precipitously for CP700 upon increasing the calcination temperature to an SBET of 9.73 m2/g and pore volume of 0.025 cm3/g due to annealing which created a smoother surface area as evidenced by the SEM images. UV-Vis DRS indicated CP550 had the highest band-gap (1.52 eV) which is likely due to the presence of a highly crystalline pure CaFe2O4 phase compared to the other products which existed as a mixture of Fe oxidation states evidenced by the XRD data. The PL spectra for all catalysts indicated significantly lower recombination rate for both CP550 and CP700. Introduction of IPA into the reaction mixture to eliminate hydroxyl radicals resulted in a diminishing of COD removal from 56% to 7% proving hydroxyl radicals to be the primary reactive species responsible for photodegradation of POME.