ABSTRACT
Fine tuning of the metal site coordination environment of a single-atom catalyst (SAC) to boost its catalytic activity for oxygen reduction reaction (ORR) is of significance but challenging. Herein, we report a new SAC bearing Fe-N3C-N sites with asymmetric in-plane coordinated Fe-N3C and axial coordinated N atom for ORR, which was obtained by pyrolysis of an iron isoporphyrin on polyvinylimidazole (PVI) coated carbon black. The C@PVI-(NCTPP)Fe-800 catalyst exhibited significantly improved ORR activity (E1/2 = 0.89 V vs RHE) than the counterpart SAC with Fe-N4-N sites in 0.1 M KOH. Significantly, the Zn-air batteries equipped with the C@PVI-(NCTPP)Fe-800 catalyst demonstrated an open-circuit voltage (OCV) of 1.45 V and a peak power density (Pmax) of 130 mW/cm2, outperforming the commercial Pt/C catalyst (OCV = 1.42 V; Pmax = 119 mW/cm2). The density functional theory (DFT) calculations revealed that the d-band center of the asymmetric Fe-N3C-N structure shifted upward, which enhances its electron-donating ability, favors O2 adsorption, and supports O-O bond activation, thus leading to significantly promoted catalytic activity. This research presents an intriguing strategy for the designing of the active site architecture in metal SACs with a structure-function controlled approach, significantly enhancing their catalytic efficiency for the ORR and offering promising prospects in energy-conversion technologies.
ABSTRACT
Bioinspired by the active sites of multicopper oxidases (MCOs), bi/multinuclear copper complexes have attracted great attention in promoting catalytic activity for the oxygen reduction reaction (ORR). Herein, we report the preparation of a Cu-N-C electrocatalyst Cu-BPOZ@CNB-400 for efficient ORR, which was obtained by low temperature pyrolysis of a dinuclear 2,5-bis(2-pyridyl)-1,3,4-oxadiazole (BPOZ) copper complex loaded on a N-doped carbon support at 400 °C. Cu-BPOZ@CNB-400 exhibited a half-wave potential (E1/2) of 0.86 V vs. RHE for the ORR in 0.1 M KOH solution, which was significantly higher than that of the Cu-BPOZ@CNB-800 (E1/2 = 0.83 V) catalyst treated under high temperature (at 800 °C) and the control catalyst Cu-Phen@CNB-400 (E1/2 = 0.82 V) derived from low-temperature-treatment (at 400 °C) of a mononuclear phenanthroline-coordinated-Cu complex loaded on a N-doped carbon support. When Cu-BPOZ@CNB-400 was applied as the cathode catalyst in zinc-air batteries a maximum power density (Pmax) of 127 mW cm-2 could be achieved, demonstrating comparable catalyst performance to the commercial 20 wt% Pt/C (Pmax = 122 mW cm-2) and the control Cu-Phen@CNB-400 catalyst (Pmax = 105 mW cm-2) under similar experimental conditions. Low-temperature pyrolysis of dinuclear copper complexes on a carbon support improved the charge transfer efficiency, inhibited metal aggregation, and could produce highly dispersed Cu-N-C catalysts with dinuclear copper sites for promoting the 4e--reduction selectivity of the ORR. It thus provides a cost-effective approach for the controllable fabrication of efficient ORR catalysts to be applied for energy conversion devices.
ABSTRACT
A P-doped PtNi alloy loaded on N,C-doped TiO2 nanosheets (P-PtNi@N,C-TiO2) exhibited excellent activity and durability for the oxygen reduction reaction (ORR) in 0.1 M HClO4 solution with mass (4×) and specific (6×) activity several times higher than those of commercial 20 wt% Pt/C, respectively. The P dopant mitigated the dissolution of Ni and strong interactions between the catalyst and the N,C-TiO2 support inhibited catalyst migration. This provides a new approach for the design of high-performance non-carbon-supported low-Pt catalysts to be used in harsh acidic environments.