ABSTRACT
Mn ferrite (MnFe(2)O(4)) nanoparticles, having diameters from 4 to 50 nm, were synthesized using a modified co-precipitation technique in which mixed metal chloride solutions were added to different concentrations of boiling NaOH solutions to control particle growth rate. Thermomagnetization measurements indicated an increase in Néel temperature corresponding to increased particle growth rate and particle size. The Néel temperature is also found to increase inversely proportionally to the cation inversion parameter, delta, appearing in the formula (Mn(1-delta)Fe(delta))(tet)[Mn(delta)Fe(2-delta)](oct)O(4). These results contradict previously published reports of trends between Néel temperature and particle size, and demonstrate the dominance of cation inversion in determining the strength of superexchange interactions and subsequently Néel temperature in ferrite systems. The particle surface chemistry, structure, and magnetic spin configuration play secondary roles.
Subject(s)
Crystallization/methods , Manganese/chemistry , Nanoparticles/chemistry , Nanoparticles/ultrastructure , Nanotechnology/methods , Cations , Fractional Precipitation , Macromolecular Substances/chemistry , Materials Testing , Molecular Conformation , Particle Size , Surface Properties , TemperatureABSTRACT
Cobalt ferrite particles with diameters ranging from a few micrometer to about 15 nm were synthesized using a modified oxidation process. The fine control of the particle size was achieved by introducing various concentrations of Fe(3+) ions at the beginning of the reaction. Among the particle sizes obtained by using this method, particles with a grain size of about 36 nm showed a magnetization (M(s)) of 64 emu/g and a maximum coercivity (H(c)) of 2020 Oe at room temperature. The corresponding squareness ratio was found to be 0.53.