Influence of the Thermal Conductivity of Thermally Conductive Plastics on the Thermal Distribution of an Light-Emitting Diode Headlight for Vehicles.

This paper investigates the thermal distribution of an LED headlight for vehicles based on the thermal conductivity of thermally conductive plastics (TCP). In general, heat dissipation structures used for LED headlights are made from metallic materials. However, headlight structures made from TCP have not been investigated. The headlights made from TCP having a various thermal conductivity were fabricated by injection molding with and without a metal plate insert. The temperature characteristics were compared and analyzed using thermal simulations and measurement. The inserted metal in TCP greatly reduced the temperature at solder point, indicating that the fast heat dissipation from the high power LED package to TCP though the inserted metal is essential. The measured temperature at solder points decreased as the thermal conductivity of TCP increased, which is well matched to the simulation results. The measured temperature at the solder point was lower than 150 °C when the thermal conductivity of the TCP was 10 W/mK.

Opposite Behavior of Multilayer Graphene/ Indium-Tin-Oxide p-Electrode for Gallium Nitride Based-Light Emitting Diodes Depending on Thickness of Indium-Tin-Oxide Layer.

In order to improve EQE, we have investigated on the role of multilayer graphene (MLG) on the electrical and optical properties of GaN based light-emitting diodes (LEDs) with ultrathin ITO (5 nm or 10 nm)/p-GaN contacts. The MLG was transferred on the ITO/p-GaN to decrease sheet resistance of thin ITO p-electrode and improve the current spreading of LEDs. The LEDs with the ITO 5 nm and MLG/ITO 5 nm structures showed 3.25 and 3.06 V at 20 mA, and 11.69 and 13.02 mW/sr at 400 mA, respectively. After forming MLG on ITO 5 nm, the electro-optical properties were enhanced. Furthermore, the GaN based-LEDs applied to the ITO 10 nm, and MLG/ITO (10 nm) structures showed 2.95 and 3.06 V at 20 mA, and 20.28 and 16.74 mW/sr at 400 mA, respectively. The sheet resistance of the MLG transferred to ITO 5 nm was decreased approximately four fold compared to ITO 5 nm. On the other hand, the ITO 10 nm and MLG/ITO 10 nm showed a similar sheet resistance; the transmittance of the LEDs with ITO 10 nm decreased to 16% due to MLG formation on ITO. This suggests that the relationship between the sheet resistance and transmittance according to the ITO film thickness affected the electro-optical properties of the LEDs with a transparent p-electrode with the MLG/ITO dual structure.