ABSTRACT
The energy conversion efficiency (ECE) (η), current density (Jsc), open-circuit voltage (Voc), and fill factor (ff) of perovskite solar cells were studied by using the transmittance of a nanopatterned mesoporous TiO2 (mp-TiO2) thin-film layer. To improve the ECE of perovskite solar cells, a mp-TiO2 thin-film layer was prepared to be used as an electron transport layer (ETL) via the nanoimprinting method for nanopatterning, which was controlled by the aspect ratio. The nanopatterned mp-TiO2 thin-film layer had a uniform and well-designed structure, and the diameter of nanopatterning was 280 nm. The aspect ratio was controlled at the depths of 75, 97, 127, and 167 nm, and the perovskite solar cell was fabricated with different depths. The ECE of the perovskite solar cells with the nanopatterned mp-TiO2 thin-film layer was 14.50%, 15.30%, 15.83%, or 14.24%, which is higher than that of a non-nanopatterned mp-TiO2 thin-film layer (14.07%). The enhancement of ECE was attributed to the transmittance of the nanopatterned mp-TiO2 thin-film layer that is due to the improvement of the electron generation. As a result, better electron generation affected the electron density, and Jsc increased the Voc, and ff of perovskite solar cells.
Subject(s)
Calcium Compounds/chemistry , Oxides/chemistry , Solar Energy , Titanium/chemistryABSTRACT
The development of high efficiency dye-sensitized solar cells (DSSCs) has received tremendous attention. Many researchers have introduced new materials for use in DSSCs to achieve high efficiency. In this study, the change in power conversion efficiency (PCE) of DSSCs was investigated by introducing two types of materials-Au nanoparticles (Au NPs) and a scattering layer. A DSSC fabricated without neither Au NPs nor a scattering layer achieved a PCE of 5.85%. The PCE of a DSSC based on freestanding TiO2 nanotube arrays (f-TNTAs) with Au NPs was 6.50% due to better electron generation because the plasmonic absorption band of Au NPs is 530 nm, which matches the dye absorbance. Thus, more electrons were generated at 530 nm, which affected the PCE of the DSSC. The PCE of DSSCs based on f-TNTAs with a scattering layer was 6.61% due to better light harvesting by scattering. The scattering layer reflects all wavelengths of light that improve the light harvesting in the active layer in DSSCs. Finally, the PCE of DSSCs based on the f-TNTAs with Au NPs and a scattering layer was 7.12% due to the synergy of better electron generation and light harvesting by plasmonics and scattering. The application of Au NPs and a scattering layer is a promising research area for DSSCs as they can increase the electron generation and light harvesting ability.