Near-Surface Studies of the Changes to the Structure and Mechanical Properties of Human Enamel under the Action of Fluoride Varnish Containing CPP-ACP Compound.

Changes to the features of the enamel surface submitted to induced demineralisation and subsequent remineralisation were studied. The in vitro examination was conducted on polished slices of human molar teeth, divided in four groups: the untreated control (n = 20), challenged by a demineralisation with orthophosphoric acid (H3PO4) (n = 20), and challenged by a demineralisation following remineralisation with fluoride (F) varnish containing casein phosphopeptides (CPP) and amorphous calcium phosphate (ACP) compounds (n = 20). The specimens' enamel surfaces were subjected to analysis of structure, molecular arrangement, mechanical features, chemical composition, and crystalline organization of apatite crystals. Specimens treated with acid showed a significant decrease in crystallinity, calcium, and phosphorus levels as well as mechanical parameters, with an increase in enamel surface roughness and degree of carbonates when compared to the control group. Treatment with fluoride CPP-ACP varnish provided great improvements in enamel arrangement, as the destroyed hydroxyapatite structure was largely rebuilt and the resulting enamel surface was characterised by greater regularity, higher molecular and structural organisation, and a smoother surface compared to the demineralised one. In conclusion, this in vitro study showed that fluoride CPP-ACP varnish, by improving enamel hardness and initiating the deposition of a new crystal layer, can be an effective remineralising agent for the treatment of damaged enamel.

Evaluation of Nanocomposite Made of Polylactic Acid and Nanocellulose from Carrot Pomace Modified with Silver Nanoparticles.

In this research, it was proposed to use carrot cellulose nanofibrils (CCNF) isolated from carrot pomace modified with silver nanoparticles (AgNPs) as a filler of polylactic acid (PLA) composites matrix. The new procedure was based on two steps: first, the preparation of nanocellulose modified with metal nanoparticles, and then the combination with PLA. Two concentrations-0.25 mM and 2 mM-of AgNO3 were used to modify CCNF. Then, PLA was mixed with the filler (CCNF/AgNPs) in two proportions 99:1 and 96:4. The influence of CCNF/AgNPs on mechanical, hydrophilic, thermal, and antibacterial properties of obtained nanocomposites was evaluated. The greatest improvement of mechanical properties was observed for composite containing CCNF with 2 mM of AgNPs, which obtained the lowest Young modulus and highest strain at break. The degradation temperature was lower for PLA with CCNF/AgNPs, but crystallization temperature wasn't influenced. The addition of CCNF/AgNPs also increased hydrophilicity. The transmission rates of oxygen, nitrogen, and carbon dioxide also increased after the addition of CCNF/AgNPs to PLA. The antibacterial function against Escherichia coli and Bacillus cereus was obtained after the addition of AgNPs but only at the contact surface with the material made, suggesting the lack of migration of nanoparticles from the composite.

Surface analysis of etched enamel modified during the prenatal period.

Structural changes in the enamel surface subjected to induced demineralization and assessment of the influence of prenatal administration of ß-hydroxy ß-methylbutyrate (HMB) on enamel resistance were investigated. The examination was conducted on five sets of teeth from one-day-old spiny mice (Acomys cahirinus), one from the control and four from the experimental groups. Surface structure, molecular arrangement and crystalline organization of offspring's enamel both before and after etching were studied. Obtained results revealed that the physical and molecular arrangements of enamel were altered after the prenatal supplementation, and significantly affected its final structure and resistance against acid action. The enamel of incisors from the offspring which mothers were supplemented with HMB in a high dose (0.2 g/kgbw) and in the late period of gestation (26th-39th day) showed the highest endurance against acid treatment demonstrating only vestigial changes in their surface structure after acid action. Comparing to the remaining experimental groups, it was characterized by a reduced roughness and fractal dimension, significantly lower degree of demineralization and simultaneous lack of notable differences in the Raman spectra before and after acid etching. The results suggest that an increased enamel resiliency was the effect of a relatively high degree of mineralization and higher organization of the surface.

The effect of cadmium exposition on the structure and mechanical properties of rat incisors.

Alterations in the structure and mechanical properties of teeth in adult Wistar rats exposed to cadmium were investigated. Analyses were conducted on two sets of incisors from female and male specimens, that were intoxicated with cadmium (n = 12) or belonged to the control (n = 12). The cadmium group was administered with CdCl2 dissolved in drinking water with a dose of 4mg/kgbw for 10 weeks. The oral intake of cadmium by adult rats led to the range of structural changes in enamel morphology and its mechanical features. A significant increase of cadmium levels in the teeth in comparison to the control, a slight shift in the colour and reduction of pigmented enamel length, higher surface irregularity, a decrease of hydroxyapatite crystals size in the c-axis and simultaneous increase in pigmented enamel hardness were observed. The extent of these changes was sex-dependent and was more pronounced in males.