ABSTRACT
We have studied the dependence on the domain wall structure of the spin-transfer torque current density threshold for the onset of wall motion in curved, Gd-doped Ni(80)Fe(20) nanowires with no artificial pinning potentials. For single vortex domain walls, for both 10% and 1% Gd-doping concentrations, the threshold current density is inversely proportional to the wire width and significantly lower compared to the threshold current density measured for transverse domain walls. On the other hand for high Gd concentrations and large wire widths, double vortex domain walls are formed which require an increase in the threshold current density compared to single vortex domain walls at the same wire width. We suggest that this is due to the coupling of the vortex cores, which are of opposite chirality, and hence will be acted on by opposing forces arising through the spin-transfer torque effect.
ABSTRACT
We have used x-ray magnetic circular dichroism, which offers a unique capability to give element specific information at submonolayer sensitivity, to determine the spin and orbital magnetic moments at the Fe/GaAs(100) interface. The wedge samples, grown by molecular beam epitaxy at room temperature, consisted of 0.25-1 monolayer (ML) Fe on GaAs(100)-4x6 capped with 9 ML Co and have shown Fe spin moments of (1.84-1.96)micro(B) and a large orbital enhancement. Our results demonstrate unambiguously that the Fe/GaAs(100)-4x6 interface is ferromagnetic with a bulklike spin moment, which is highly promising for spintronics applications.