ABSTRACT
There are a limited number of methods to guide and confirm the placement of a peripherally inserted central catheter (PICC) at the cavoatrial junction. The aim of this study was to design, test and validate a dual-wavelength, diode laser-based, single optical fiber instrument that would accurately confirm PICC tip location at the cavoatrial junction of an animal heart, in vivo. This was accomplished by inserting the optical fiber into a PICC and ratiometrically comparing simultaneous visible and near-infrared reflection intensities of venous and atrial tissues found near the cavoatrial junction. The system was successful in placing the PICC line tip within 5 mm of the cavoatrial junction.
Subject(s)
Central Venous Catheters , Heart Atria , Spectrum Analysis , Vena Cava, Superior , Animals , SwineABSTRACT
The processes used to create synthetic spider silk greatly affect the properties of the produced fibers. This paper investigates the effect of process variations during artificial spinning on the thermal and mechanical properties of the produced silk. Property values are also compared to the ones of the natural dragline silk of the N. clavipes spider, and to unprocessed (as-spun) synthetic silk. Structural characterization by scanning pyroelectric microscopy is employed to provide insight into the axial orientation of the crystalline regions of the fiber and is supported by XRD data. The results show that stretching and passage through liquid baths induce crystal formation and axial alignment in synthetic fibers, but with different structural organization than natural silks. Furthermore, an increase in thermal diffusivity and elastic modulus is observed with decreasing fiber diameter, trending towards properties of natural fiber. This effect seems to be related to silk fibers being subjected to a radial gradient during production.
ABSTRACT
Spider silks have unique mechanical properties but current efforts to duplicate those properties with recombinant proteins have been unsuccessful. This study was designed to develop a single process to spin fibers with excellent and consistent mechanical properties. As-spun fibers produced were brittle, but by stretching the fibers the mechanical properties were greatly improved. A water-dip or water-stretch further increased the strength and elongation of the synthetic spider silk fibers. Given the promising results of the water stretch, a mechanical double-stretch system was developed. Both a methanol/water mixture and an isopropanol/water mixture were independently used to stretch the fibers with this system. It was found that the methanol mixture produced fibers with high tensile strength while the isopropanol mixture produced fibers with high elongation.
ABSTRACT
Spider silk has exceptional mechanical and biocompatibility properties. The goal of this study was optimization of the mechanical properties of synthetic spider silk thin films made from synthetic forms of MaSp1 and MaSp2, which compose the dragline silk of Nephila clavipes. We increased the mechanical stress of MaSp1 and 2 films solubilized in both HFIP and water by adding glutaraldehyde and then stretching them in an alcohol based stretch bath. This resulted in stresses as high as 206 MPa and elongations up to 35%, which is 4× higher than the as-poured controls. Films were analyzed using NMR, XRD, and Raman, which showed that the secondary structure after solubilization and film formation in as-poured films is mainly a helical conformation. After the post-pour stretch in a methanol/water bath, the MaSp proteins in both the HFIP and water-based films formed aligned ß-sheets similar to those in spider silk fibers.