ABSTRACT
Contemporary gas turbine engines rely on thermal barrier coatings (TBCs), which protect the structural components of the engine against degradation at extremely high operating temperatures (1300-1500 °C). The operational efficiencies of aircraft engines have seen significant improvement in recent years, primarily through the increase in operating temperatures; however, the longevity of TBCs can be potentially impacted by several types of degradation mechanisms. In this comprehensive study, a wide range of novel columnar suspension plasma sprayed (SPS) coatings were developed for their erosion, calcium-magnesium-aluminum-silicate (CMAS), and furnace cycling test (FCT) performance. Through a comprehensive investigation, the first of its kind, we achieved a range of SPS microstructures by modifying the spray parameters and measuring their microhardness, fracture toughness, column densities, and residual stresses using Raman spectroscopy. We were able to produce dendritic, lateral, branched, and columnar microstructures with a unique set of processing parameters. Coatings enhanced with a refined columnar microstructure, achieved by modulating the distance from the plasma torch, exhibited superior thermal cycling resilience. Conversely, the development of a columnar microstructure with dendritic branches, obtained by decreasing the robot's traversal speed during deposition, bolstered resistance to erosion and minimized damage from molten CMAS infiltration, thereby notably augmenting the coating's lifespan and robustness. The pursuit of the optimal columnar microstructure led to the conclusion that for each SPS coating, a general framework of optimization needs to be conducted to achieve their desired thermo-chemico-mechanical resistance as the properties required for TBCs are intertwined.
ABSTRACT
In the combustion chambers of gas turbine engines, ZrO2-8wt.%Y2O3 (YSZ) TBCs are commonly applied by air plasma spray (APS) using Ar-/H2-based plasmas via legacy torches. Alternatively, N2/H2 plasmas could be used with the potential of increasing overall deposition efficiency (DE) and hence reduce the consumption of high-value feedstock powder. Also, by increasing DE, spraying time would be reduced, thereby providing another contribution to bring down production costs. In this work, TBCs were prepared with Ar- and N2-based plasmas with different YSZ powders using Metco 9MB legacy torch. The use of N2-based plasma resulted in higher particle temperature and lower particle velocity values than those provided by the Ar-based plasma. The measured DEs were between 41-43 and 53-60% for the Ar- and N2-based plasmas, respectively. This represents a ~ 40% increase in the DE. The coatings produced with the two different plasmas exhibited equivalent porosity levels ~ 11-13%. On average, the lowest thermal conductivity values were given by a N2-based LD-B YSZ TBC. In the furnace cycle test, the performance of the TBCs prepared with the N2-based plasma was superior to that of the TBCs prepared with the Ar plasma, and also exceeding that of an industrial APS TBC benchmark.
ABSTRACT
Higher durability in thermal barrier coatings (TBCs) is constantly sought to enhance the service life of gas turbine engine components such as blades and vanes. In this study, three double layered gadolinium zirconate (GZ)-on-yttria stabilized zirconia (YSZ) TBC variants with varying individual layer thickness but identical total thickness produced by suspension plasma spray (SPS) process were evaluated. The objective was to investigate the role of YSZ layer thickness on the durability of GZ/YSZ double-layered TBCs under different thermal cyclic test conditions i.e., thermal cyclic fatigue (TCF) at 1100 °C and a burner rig test (BRT) at a surface temperature of 1400 °C, respectively. Microstructural characterization was performed using SEM (Scanning Electron Microscopy) and porosity content was measured using image analysis technique. Results reveal that the durability of double-layered TBCs decreased with YSZ thickness under both TCF and BRT test conditions. The TBCs were analyzed by SEM to investigate microstructural evolution as well as failure modes during TCF and BRT test conditions. It was observed that the failure modes varied with test conditions, with all the three double-layered TBC variants showing failure in the TGO (thermally grown oxide) during the TCF test and in the ceramic GZ top coat close to the GZ/YSZ interface during BRT. Furthermore, porosity analysis of the as-sprayed and TCF failed TBCs revealed differences in sintering behavior for GZ and YSZ. The findings from this work provide new insights into the mechanisms responsible for failure of SPS processed double-layered TBCs under different thermal cyclic test conditions.
ABSTRACT
Titanium- and chromium-based carbides are attractive coating materials to impart wear resistance. Suspension plasma spraying (SPS) is a relatively new thermal spray process which has shown a facile ability to use sub-micron and nano-sized feedstock to deposit high-performance coatings. The specific novelty of this work lies in the processing of fine-sized titanium and chromium carbides (TiC and Cr3C2) in the form of aqueous suspensions to fabricate wear-resistant coatings by SPS. The resulting coatings were characterized by surface morphology, microstructure, phase constitution, and micro-hardness. The abrasive, erosive, and sliding wear performance of the SPS-processed TiC and Cr3C2 coatings was also evaluated. The results amply demonstrate that SPS is a promising route to manufacture superior wear-resistant carbide-based coatings with minimal in situ oxidation during their processing.
ABSTRACT
A hierarchical structured composite made from clinoptilolite supported on date stones carbon is synthesized using two techniques. The composites are manufactured by fixing a natural zeolite (clinoptilolite) to the porous surface of date stones carbon or by direct hydrothermal synthesis on to the surface to provide a supported high surface area ion-exchange material for metal ion removal from aqueous streams. The fixing of the clinoptilolite is achieved using sucrose and citric acid as a binder. The composites and pure clinoptilolite were compared to test the efficacy for the removal of Sr2+ ions from an aqueous phase. The encapsulation of the Sr2+ using either vitrification or a geo-polymer addition was tested to ensure that the hazardous waste can be made safe for disposal. The hierarchical structured composites were shown to achieve a higher ion exchange capacity per gram of zeolite than the pure clinoptilolite (65mg/g for the pure natural clinoptilolite and 72mg/g for the pure synthesized clinoptilolite) with the synthesized composite (160mg/g) having higher capacity than the natural clinoptilolite composite (95mg/g). The rate at which the equilibria were established followed the same trend showing the composite structure facilitates diffusion to the ion-exchange sites in the zeolite.