Photoswitching/back-switching assessment of biobased cellulose acetate/azobenzene handleable films under visible-light LED irradiation.

The light-induced processes performed by photofunctional polymer films are crucial aspects of developing integrated energy storage devices properly. Herein, we report the preparation, characterization, and study of the optical properties of a series of biobased cellulose acetate/azobenzene (CA/Az1) handleable films at different compositions. The photoswitching/back-switching behavior of the samples was investigated using varied LED irradiation sources. Additionally, poly(ethylene glycol) (PEG) was deposited onto cellulose acetate/azobenzene films to study the back-switching process's effect and nature in the fabricated films. Interestingly, the melting enthalpies of PEG before and after being irradiated with blue LED light were 2.5 mJ and 0.8 mJ, respectively. Conveniently, FTIR and UV-visible spectroscopy, thermogravimetry (TGA), contact angle, differential scanning calorimetry (DSC), polarized light microscopy (PLM), and atomic force microscopy (AFM) were used for the characterization of the sample films. Complementarily, theoretical electronic calculations provided a consistent approach to the energetic change in the dihedral angles and non-covalent interaction for the trans and cis isomer in the presence of cellulose acetate monomer. The results of this study revealed that CA/Az1 films are viable photoactive materials displaying handleability attributes with potential uses in harvesting, converting, and storing light energy.

A facile approach for tuning optical and surface properties of novel biobased Alginate/POTE handleable films via solvent vapor exposure.

Novel biobased films consisting of alginate blends with poly (octanoic acid 2-thiophen-3-yl-ethyl ester) (POTE), a conducting polymer, were prepared by solution casting, and their optical, morphological, thermal, and surface properties were studied. Using UV-visible spectroscopy, atomic force microscopy (AFM), and scanning electron microscopy (SEM), the effects of tetrahydrofuran solvent vapors on the optical properties and surface morphology of biobased films with different POTE contents were studied. Results indicate that morphological rearrangements of POTE take place during the process of solvent exposure. Specifically, the solvent vapor induced the formation of POTE small crystalline domains, which allows envisioning the potential of tuning UV-visible absorbance and wettability behavior of biobased films. Finally, theoretical electronic calculations (specifically frontier molecular orbitals analysis) provided consistent evidence on POTE's preferential orientation and selectivity toward the THF-vapor medium.