Scalable Synthesis of High-Quality Ultrathin Ferroelectric Magnesium Molybdenum Oxide.

The development of ultrathin, stable ferroelectric materials is crucial for advancing high-density, low-power electronic devices. Nonetheless, ultrathin ferroelectric materials are rare due to the critical size effect. Here, a novel ferroelectric material, magnesium molybdenum oxide (Mg2Mo3O8) is presented. High-quality ultrathin Mg2Mo3O8 crystals are synthesized using chemical vapor deposition (CVD). Ultrathin Mg2Mo3O8 has a wide bandgap (≈4.4 eV) and nonlinear optical response. Mg2Mo3O8 crystals of varying thicknesses exhibit out-of-plane ferroelectric properties at room temperature, with ferroelectricity retained even at a 2 nm thickness. The Mg2Mo3O8 exhibits a relatively large remanent polarization ranging from 33 to 52 µC cm- 2, which is tunable by changing its thickness. Notably, Mg2Mo3O8 possesses a high Curie temperature (>980 °C) across various thicknesses. Moreover, the as-grown Mg2Mo3O8 crystals display remarkable stability under harsh environments. This work introduces nolanites-type crystal into ultrathin ferroelectrics. The scalable synthesis of stable ultrathin ferroelectric Mg2Mo3O8 expands the scope of ferroelectric materials and may prosper applications of ferroelectrics.

Ion adsorption promotes Frank-van der Merwe growth of 2D transition metal tellurides.

Reliable synthesis methods for high-quality, large-sized, and uniform two-dimensional (2D) transition-metal dichalcogenides (TMDs) are crucial for their device applications. However, versatile approaches to growing high-quality, large-sized, and uniform 2D transition-metal tellurides are rare. Here, we demonstrate an ion adsorption strategy that facilitates the Frank-van der Merwe growth of 2D transition-metal tellurides. By employing this method, we grow MoTe2 and WTe2 with enhanced lateral size, reduced thickness, and improved uniformity. Comprehensive characterizations confirm the high quality of as-grown MoTe2. Moreover, various characterizations verify the adsorption of K+ and Cl- ions on the top surface of MoTe2. X-ray photoelectron spectroscopy (XPS) analysis reveals that the MoTe2 is stoichiometric without K+ and Cl- ions and exhibits no discernable oxidation after washing. This top surface control strategy provides a new controlling knob to optimize the growth of 2D transition-metal tellurides and holds the potential for generalized to other 2D materials.