Technology and Properties of Peripheral Laser-Welded Micro-Joints.

This article presents the results of research on the technology and peripheral properties of laser-welded micro-couplings. The aim of this research was to determine the characteristics of properly made joints and to indicate the range of optimal parameters of the welding process. Thin-walled AISI 316L steel pipes with diameters of 1.5 and 2 mm used in medical equipment were tested. The micro-welding process was carried out on a SISMA LM-D210 Nd:YAG laser. The research methods used were macroscopic and microscopic analyses of the samples, and assessment of the distribution of elements in the weld, the distribution of microhardness and the tear strength of the joint. As a result of the tests, the following welding parameters are recommended: a pulse energy of 2.05 J, pulse duration of 4 ms and frequency of 2 Hz, beam focusing to a diameter of 0.4 mm and a rotation speed of 0.157 rad/s. In addition, the tests show good joint properties with a strength of more than 75% of the thinner pipe, uniform distribution of alloying elements and a complex dendritic structure characteristic of pulse welding.

Semi-Hybrid CO2 Laser Metal Deposition Method with Inter Substrate Buffer Zone.

This article presents the results of the metal deposition process using additive materials in the form of filler wire and metal powder. An important problem in wire deposition using a CO2 laser was overcome by using a combination of the abovementioned methods. The deposition of a multicomponent alloy-Inconel 625-on a basic substrate such as structural steel is presented. The authors propose a new approach for stopping carbon and iron diffusion from the substrate, by using the Semi-Hybrid Deposition Method (S-HDM) developed by team members. The proposed semi-hybrid method was compared with alternative wire and powder deposition using laser beam. Differences of S-HDM and classic wire deposition and powder deposition methods are presented using metallographic analysis, within optic and electron microscopy. Significant differences in the obtained results reveal advantages of the developed method compared to traditional deposition methods. A comparison of the aforementioned methods performed using nickel based super alloy Inconel 625 deposited on low carbon steel substrate is presented. An alternative prototyping approach for an advanced high alloy materials deposition using CO2 laser, without the requirement of using the same substrate was presented in this article. This study confirmed the established assumption of reducing selected components diffusion from a substrate via buffer layer. Results of metallographic analysis confirm the advantages and application potential of using the new semi-hybrid method for prototyping high alloy materials on low alloy structural steel substrate.

Microstructure and Properties of Inconel 625 Fabricated Using Two Types of Laser Metal Deposition Methods.

The effect of using two different deposition systems on the microstructure and mechanical properties was studied in this paper. For this purpose, laser-engineered net shaping (LENS) and high-power CO2 laser deposition processes were applied to fabricate Inconel 625 samples. The microstructure of the Inconel 625 produced by both additive techniques was characterized using light microscopy (LM), scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM). The mechanical properties were characterized by tensile tests and microhardness measurements. High-power laser application resulted in a strong <100> build texture, while, at low powers, the {011} <100> Goss component increased. Both types of deposited materials showed dendritic microstructures with Ti-, Mo-, and Nb-rich zones at the cell boundaries, where numerous precipitates (Nb2C, NbC, titanium carbides, Nb3Ni, and NbNiCr) were also observed. It was also noted that both variants were characterized by the same slope with a proportional length, but the Inconel 625 fabricated via LENS showed a higher average yield strength (YS; 524 MPa vs. 472 MPa) and ultimate tensile strength (UTS; 944 MPa vs. 868 MPa) and lower elongation (35% vs. 42%) than samples obtained with the high-power CO2 laser deposition process.

Steel Sheets Laser Lap Joint Welding-Process Analysis.

This article presents the results of steel-sheet lap-joint-welding using laser beam radiation. The use of a laser beam and keyhole effect for deep material penetration in lap joint welding was presented. Thermodynamic mechanism of laser welding is related to material properties and process parameters. Estimation of welding parameters and joint properties' analysis was performed through numerical simulation. The article presents a possibility of modeling laser lap-joint welding by using Simufact Welding software based on Marc solver and thermo-mechanical solution. Numerical calculation was performed for surface and conical volumetric heat sources simulating laser absorption and keyhole effect during steel sheet welding. Thermo-mechanical results of fusion zone (FZ), heat-affected zone (HAZ) and phase transformations calculated in numerical simulation were analyzed. The welding parameters for partial sealed joint penetration dedicated for gas piping installations were estimated from the numerical analysis. Low-carbon constructional steel was used for numerical and experimental analyses. A trial joint based on the estimated parameters was prepared by using a CO2 laser. Numerical and experimental results in the form of hardness distributions and weld geometry were compared. Metallographic analysis of the obtained weld was presented, including crystallographic structures and inclusions in the cross section of the joint.

Numerical and Metallurgical Analysis of Laser Welded, Sealed Lap Joints of S355J2 and 316L Steels under Different Configurations.

This paper presents the results of laser welding of dissimilar joints, where low-carbon and stainless steels were welded inthe lap joint configuration. Performed welding of austenitic and ferritic-pearlitic steels included a sealed joint, where only partial penetration of lower material was obtained.The authors presented acomparative study of the joints under different configurations. The welding parameters for the assumed penetration were estimated via anumericalsimulation. Moreover, a stress-strain analysis was performed based on theestablished model. Numerical analysis showed significant differences in joint properties, therefore, further study was conducted. Investigation of the fusion mechanism in the obtained joints wascarried out using electron dispersive spectroscopy (EDS) and metallurgical analysis. The study of the lap joint under different configurations showed considerable dissimilarities in stress-strain distribution and relevant differences in the fusion zone structure. The results showed advantages of using stainless steel as the upper material of a microstructure, and uniform chemical element distribution and stress analysis is considered.