Unrevealing tunable resonant excitons and correlated plasmons and their coupling in new amorphous carbon-like for highly efficient photovoltaic devices.

An understanding on roles of excitons and plasmons is important in excitonic solar cells and photovoltaic (PV) technologies. Here, we produce new amorphous carbon (a-C) like films on Indium Tin Oxide (ITO) generating PV cells with efficiency three order of magnitude higher than the existing biomass-derived a-C. The amorphous carbon films are prepared from the bioproduct of palmyra sap with a simple, environmentally friendly, and highly reproducible method. Using spectroscopic ellipsometry, we measure simultaneously complex dielectric function, loss function as well as reflectivity and reveal coexistence of many-body resonant excitons and correlated-plasmons occurring due to strong electronic correlations. X-ray absorption and photoemission spectroscopies show the nature of electron and hole in defining the energy of the excitons and plasmons as a function of N or B doping. Our result shows new a-C like films and the importance of the coupling of resonant excitons and correlated plasmons in determining efficiency of photovoltaic devices.

Phase-sensitive order parameter symmetry test experiments utilizing Nd(2-x)Ce(x)CuO(4-y)/Nb zigzag junctions.

Phase-sensitive order parameter symmetry test experiments are presented on the electron-doped high-T(c) cuprate Nd(2-x)Ce(x)CuO(4-y). These experiments have been conducted using zigzag-shaped thin film Josephson structures, in which the Nd(2-x)Ce(x)CuO(4-y) is connected to the low-T(c) superconductor Nb via an Au barrier layer. For the optimally doped as well as for the overdoped Nd(2-x)Ce(x)CuO(4-y), a clear predominant d(x2-y2)-wave behavior is observed at T=4.2 K. Both compounds were also investigated at T=1.6 K, presenting no indications for a change to a predominant s-wave symmetry with decreasing temperature.