ABSTRACT
Smart pH-responsive superabsorbent polymers (SAPs) could be useful for self-healing of cracks in mortar. They will swell minimally during the alkaline conditions of mixing, leading to only small macro-pores but will swell stronger with a lower pH when water enters the cracks. As such, polysaccharides (alginate, chitosan and agarose) were methacrylated and cross-linked with amine-based monomers (dimethylaminoethyl methacrylate and dimethylaminopropyl methacrylamide) to induce a varying pH-sensitivity. These materials showed a strong cross-linking efficiency and induced moisture uptake capacities up to 122% at 95% relative humidity with a negligible hysteresis. Additionally, interesting pH-responsive swelling capacities were obtained, especially for SAPs based on chitosan and agarose with values up to 110gwater/gSAP. Most of these materials showed limited hydrolysis in cement filtrate solutions, making them very promising for use in mortar.
ABSTRACT
Polysaccharides, and especially alginate, can be useful for self-healing of cracks in concrete. Instead of weak electrostatic bonds present within calcium alginate, covalent bonds, by methacrylation of the polysaccharides, will result in mechanically stronger superabsorbent polymers (SAPs). These methacrylated alginate chains as backbone are combined with two acrylic monomers in a varying molar fraction. These SAPs show a moisture uptake capacity up to 110% their own weight at a relative humidity of 95%, with a negligible hysteresis. The swelling capacity increased (up to 246 times its own weight) with a decreasing acrylic acid/2 acrylamido-2-methylpropane sulfonic acid ratio. The SAPs also showed a thermal stability up to 200°C. Interestingly, the SAP composed of alginate and acrylic acid exerted a very limited decrease in compressive strength (up to 7% with addition of 1wt% SAP) rendering this material interesting for the envisaged self-healing application.