ABSTRACT
Considering the increasing amount of water pollution, nanocomposite advances for the effective elimination of hazardous pollutants are still needed. α-Fe2O3, Cr0·5Fe1·5O3 and CrFeO3 nanoparticles were synthesized via an eco-friendly material synthesis i. e hydrothermal route without using any precipitating agent and were studied to remove congo-red dye using photocatalytic properties. X-ray diffraction (XRD), Transmission electron microscopy (TEM), Field emission scanning electron microscopy (FESEM), Fourier transform infrared spectroscopy (FESEM), Brunauer-Emmett-Teller (BET), X-ray photoelectron spectroscopy (XPS) characterizations have been performed to know about the material structure and properties of synthesized samples. High efficiency (95.2%) of degradation was achieved under sunlight using a very low amount of CrFeO3 catalyst (0.2 g/L) at a 6-pH level of dye and was confirmed using UV spectroscopy, TOC (84%), LC-HRMS. Also, the potential to degrade the CR dye was concluded from the high rate of BOD5/COD. The results showed a significant enhancement in the degradation of α-Fe2O3 from 52.3% to 95.2% in a short duration of 15 min by introducing chromium as a dopant. The doping of chromium influenced the major factors responsible for the photocatalytic activity such as the increase in range of absorbance, increased e--h+ pair separation, improvement in the charge transfer process and active site formation which significantly enhanced the process of degradation. We found that the Cr-doped α-Fe2O3 nanomaterial could effectively remove dyes, such as congo-red, from industrial water-waste.