Chitosan as capping agent in a robust one-pot procedure for a magnetic catalyst synthesis.

Here, we report a one-pot solvothermal method for the development of magnetically recoverable catalysts with Ru or Ag nanoparticles (NPs) capped by chitosan (CS), a derivative of natural chitin. The formation of iron oxide NPs was carried out in situ in the presence of CS and iron acetylacetonate in boiling triethyleneglycol (TEG) due to CS solubilization in warm TEG. Coordination with Ru or Ag species and the NP formation take place in the same reaction solution, eliminating intermediate steps. In optimal conditions the method developed allows stabilization of 2.2 nm monodisperse Ru NPs (containing both Ru0 and Ru4+ species) that are evenly distributed through the catalyst, while for Ag NPs, this stabilizing medium is inferior, leading to exceptionally large Ag nanocrystals. Catalytic testing of CS-Ru magnetically recoverable catalysts in the reduction of 4-nitrophenol to 4-aminophenol with excess NaBH4 revealed that the catalyst with 2.2 nm Ru NPs exhibits the highest catalytic activity compared to samples with larger Ru NPs (2.9-3.2 nm). Moreover, this catalyst displayed extraordinary shelf-life in the aqueous solution (up to ten months) and excellent reusability in ten consecutive reactions with easy magnetic separation at each step which were assigned to its conformational rigidity at a constant pH. These characteristics as well as favorable environmental factors of the catalyst fabrication, make it promising for nitroarene reduction.

Facile Synthesis of Magnetically Recoverable Pd and Ru Catalysts for 4-Nitrophenol Reduction: Identifying Key Factors.

This paper reports the development of robust Pd- and Ru-containing magnetically recoverable catalysts in a one-pot procedure using commercially available, branched polyethyleneimine (PEI) as capping and reducing agent. For both catalytic metals, ∼3 nm nanoparticles (NPs) are stabilized in the PEI shell of magnetite NPs, whose aggregation allows for prompt magnetic separation. The catalyst properties were studied in a model reaction of 4-nitrophenol hydrogenation to 4-aminophenol with NaBH4. A similar catalytic NP size allowed us to decouple the NP size impact on the catalytic performance from other parameters and to follow the influence of the catalytic metal type and amount as well as the PEI amount on the catalytic activity. The best catalytic performances, the 1.2 min-1 rate constant and the 433.2 min-1 turnover frequency, are obtained for the Ru-containing catalyst. This is discussed in terms of stability of Ru hydride facilitating the surface-hydrogen transfer and the presence of Ru4+ species on the Ru NP surface facilitating the nitro group adsorption, both leading to an increased catalyst efficiency. High catalytic activity as well as the high stability of the catalyst performance in five consecutive catalytic cycles after magnetic separation makes this catalyst promising for nitroarene hydrogenation reactions.